EN 10088-3 X2CrCuNiN23-2-2 vs EN 10088-1 X2CrNiN22-2

Close Alternative — 83.5% match based on chemical composition and mechanical property overlap.

EN 10088-3 X2CrCuNiN23-2-2 (EN 10088-3:2014) and EN 10088-1 X2CrNiN22-2 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X2CrCuNiN23-2-2 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X2CrNiN22-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X2CrCuNiN23-2-2 vs EN 10088-1 X2CrNiN22-2 is a 83.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 83.5%.

Frequently Compared With EN 10088-3 X2CrCuNiN23-2-2:
ASTM A959 2304 EN 10088-1 1.4301 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4845
Match Breakdown
CHEMISTRY MATCH
83.5%
MECHANICAL MATCH
No shared data
OVERALL
83.5%
Specifications
Property EN 10088-3 X2CrCuNiN23-2-2 EN 10088-1 X2CrNiN22-2
Standard EN 10088-3:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.045 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) 1.00-3.00 <=2.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.010
Cr (%) 21.5-24.0 21.5-24.0
Mo (%) <=0.50 <=0.45
Ni (%) 1.00-3.00 1.00-2.90
N (%) 0.12-0.20 0.16-0.28
Cu (%) 1.60-3.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X2CrCuNiN23-2-2 EN 10088-1 X2CrNiN22-2
Tensile Strength 650-900 MPa Not specified
Yield Strength >=400 MPa Not specified
Elongation >=25% Not specified
Hardness <=300 HB Not specified
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X2CrCuNiN23-2-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X2CrNiN22-2
Not documented
Key Differences
Can EN 10088-3 X2CrCuNiN23-2-2 Be Substituted With EN 10088-1 X2CrNiN22-2?
EN 10088-3 X2CrCuNiN23-2-2 and EN 10088-1 X2CrNiN22-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-3 X2CrCuNiN23-2-2
0 active listings and RFQs →
EN 10088-1 X2CrNiN22-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X2CrCuNiN23-2-2 and EN 10088-1 X2CrNiN22-2?
EN 10088-3 X2CrCuNiN23-2-2 specifies Cu which is not specified for EN 10088-1 X2CrNiN22-2.
Can EN 10088-3 X2CrCuNiN23-2-2 be substituted with EN 10088-1 X2CrNiN22-2?
EN 10088-3 X2CrCuNiN23-2-2 and EN 10088-1 X2CrNiN22-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.