EN 10088-3 X2CrMoTiS18-2 vs EN 10088-1 X2CrMoTi29-4

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-3 X2CrMoTiS18-2 (EN 10088-3:2014) and EN 10088-1 X2CrMoTi29-4 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X2CrMoTiS18-2 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X2CrMoTi29-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X2CrMoTiS18-2 vs EN 10088-1 X2CrMoTi29-4 is a 69.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-3 X2CrMoTiS18-2:
IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
69.9%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-3 X2CrMoTiS18-2 EN 10088-1 X2CrMoTi29-4
Standard EN 10088-3:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.025
Si (%) <=1.00 <=1.00
Mn (%) <=0.50 <=1.00
P (%) <=0.040 <=0.030
S (%) 0.15-0.35 <=0.010
Cr (%) 17.5-19.0 28.0-30.0
Mo (%) 2.00-2.50 3.50-4.50
Ti (%) <=0.80 Not specified
N (%) Not specified <=0.045
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X2CrMoTiS18-2 EN 10088-1 X2CrMoTi29-4
Tensile Strength 430-600 MPa Not specified
Yield Strength >=280 MPa Not specified
Elongation >=15% Not specified
Hardness <=200 HB Not specified
Condition Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X2CrMoTiS18-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X2CrMoTi29-4
Not documented
Key Differences
Can EN 10088-3 X2CrMoTiS18-2 Be Substituted With EN 10088-1 X2CrMoTi29-4?
EN 10088-3 X2CrMoTiS18-2 and EN 10088-1 X2CrMoTi29-4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-3 X2CrMoTiS18-2
0 active listings and RFQs →
EN 10088-1 X2CrMoTi29-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X2CrMoTiS18-2 and EN 10088-1 X2CrMoTi29-4?
EN 10088-3 X2CrMoTiS18-2 specifies Ti which is not specified for EN 10088-1 X2CrMoTi29-4. EN 10088-1 X2CrMoTi29-4 specifies N which is not specified for EN 10088-3 X2CrMoTiS18-2.
Can EN 10088-3 X2CrMoTiS18-2 be substituted with EN 10088-1 X2CrMoTi29-4?
EN 10088-3 X2CrMoTiS18-2 and EN 10088-1 X2CrMoTi29-4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.