Strong Match — 88.4% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X2CrMoTiS18-2 (EN 10088-3:2014) and IS 6603 X02Cr18Mo2TiS (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X2CrMoTiS18-2 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while IS 6603 X02Cr18Mo2TiS is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
EN 10088-3 X2CrMoTiS18-2 is defined under European Standard (EN), originating from Europe, while IS 6603 X02Cr18Mo2TiS is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-3 X2CrMoTiS18-2 vs IS 6603 X02Cr18Mo2TiS is a 95.1% match.
As per mechanical properties, the match is 75%.
Combined, this makes them a strong match overall at 88.4%.
Frequently Compared With EN 10088-3 X2CrMoTiS18-2:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X2CrMoTiS18-2
IS 6603 X02Cr18Mo2TiS
Tensile Strength
430-600 MPa
>=430 MPa
Yield Strength
>=280 MPa
>=280 MPa
Elongation
>=15%
>=15%
Hardness
<=200 HB
<=200 HB
Condition
Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; Tensile Strength is a minimum as printed
Typical Applications
EN 10088-3 X2CrMoTiS18-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
IS 6603 X02Cr18Mo2TiS
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-3 X2CrMoTiS18-2 Be Substituted With IS 6603 X02Cr18Mo2TiS?
EN 10088-3 X2CrMoTiS18-2 and IS 6603 X02Cr18Mo2TiS overlap closely enough on chemistry and mechanical properties that IS 6603 X02Cr18Mo2TiS is often considered as a substitute for EN 10088-3 X2CrMoTiS18-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-3 X2CrMoTiS18-2 and IS 6603 X02Cr18Mo2TiS?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-3 X2CrMoTiS18-2 be substituted with IS 6603 X02Cr18Mo2TiS?
EN 10088-3 X2CrMoTiS18-2 and IS 6603 X02Cr18Mo2TiS overlap closely enough on chemistry and mechanical properties that IS 6603 X02Cr18Mo2TiS is often considered as a substitute for EN 10088-3 X2CrMoTiS18-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.