Minimal Match — 43.4% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X2CrNi18-9 (EN 10088-3:2014) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X2CrNi18-9 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications.
EN 10088-3 X2CrNi18-9 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10088-3 X2CrNi18-9 vs GOST 5632 06Kh23N28 is a 65.1% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 43.4%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X2CrNi18-9
GOST 5632 06Kh23N28
Tensile Strength
500-700 MPa
≥510 MPa
Yield Strength
>=175 MPa
≥196 MPa
Elongation
>=45%
≥35%
Hardness
<=215 HB
Not specified
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Not specified
Max Service Temp
Not specified
1050°C
Typical Applications
EN 10088-3 X2CrNi18-9
General purposes, semi-finished products, bars, rods, wire, sections and bright products
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
EN 10088-3 X2CrNi18-9 specifies P, S, N which are not specified for GOST 5632 06Kh23N28.
Can EN 10088-3 X2CrNi18-9 Be Substituted With GOST 5632 06Kh23N28?
EN 10088-3 X2CrNi18-9 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-3 X2CrNi18-9 and GOST 5632 06Kh23N28?
EN 10088-3 X2CrNi18-9 specifies P, S, N which are not specified for GOST 5632 06Kh23N28.
Can EN 10088-3 X2CrNi18-9 be substituted with GOST 5632 06Kh23N28?
EN 10088-3 X2CrNi18-9 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.