EN 10088-3 X2CrNiMnMoN25-18-6-5 vs EN 10088-1 X2CrNiMnMoN25-18-6-5

Strong Match — 100% match based on chemical composition and mechanical property overlap.

EN 10088-3 X2CrNiMnMoN25-18-6-5 (EN 10088-3:2014) and EN 10088-1 X2CrNiMnMoN25-18-6-5 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X2CrNiMnMoN25-18-6-5 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X2CrNiMnMoN25-18-6-5 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X2CrNiMnMoN25-18-6-5 vs EN 10088-1 X2CrNiMnMoN25-18-6-5 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With EN 10088-3 X2CrNiMnMoN25-18-6-5:
GOST 5632 08X18H10 EN 10088-1 1.4301 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property EN 10088-3 X2CrNiMnMoN25-18-6-5 EN 10088-1 X2CrNiMnMoN25-18-6-5
Standard EN 10088-3:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) 5.0-7.0 5.0-7.0
P (%) <=0.030 <=0.030
S (%) <=0.015 <=0.015
Cr (%) 24.0-26.0 24.0-26.0
Mo (%) 4.0-5.0 4.0-5.0
Ni (%) 16.0-19.0 16.0-19.0
N (%) 0.30-0.60 0.30-0.60
Nb (%) <=0.15 <=0.15
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X2CrNiMnMoN25-18-6-5 EN 10088-1 X2CrNiMnMoN25-18-6-5
Tensile Strength 800-950 MPa Not specified
Yield Strength >=420 MPa Not specified
Elongation >=35% Not specified
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X2CrNiMnMoN25-18-6-5
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X2CrNiMnMoN25-18-6-5
Not documented
Can EN 10088-3 X2CrNiMnMoN25-18-6-5 Be Substituted With EN 10088-1 X2CrNiMnMoN25-18-6-5?
EN 10088-3 X2CrNiMnMoN25-18-6-5 and EN 10088-1 X2CrNiMnMoN25-18-6-5 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMnMoN25-18-6-5 is often considered as a substitute for EN 10088-3 X2CrNiMnMoN25-18-6-5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-3 X2CrNiMnMoN25-18-6-5
0 active listings and RFQs →
EN 10088-1 X2CrNiMnMoN25-18-6-5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X2CrNiMnMoN25-18-6-5 and EN 10088-1 X2CrNiMnMoN25-18-6-5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-3 X2CrNiMnMoN25-18-6-5 be substituted with EN 10088-1 X2CrNiMnMoN25-18-6-5?
EN 10088-3 X2CrNiMnMoN25-18-6-5 and EN 10088-1 X2CrNiMnMoN25-18-6-5 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNiMnMoN25-18-6-5 is often considered as a substitute for EN 10088-3 X2CrNiMnMoN25-18-6-5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.