EN 10088-3 X2CrNiMoCuWN25-7-4 vs GOST 5632 06Kh23N28
Minimal Match — 31% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X2CrNiMoCuWN25-7-4 (EN 10088-3:2014) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X2CrNiMoCuWN25-7-4 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications.
EN 10088-3 X2CrNiMoCuWN25-7-4 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10088-3 X2CrNiMoCuWN25-7-4 vs GOST 5632 06Kh23N28 is a 46.5% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 31%.
Frequently Compared With EN 10088-3 X2CrNiMoCuWN25-7-4:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X2CrNiMoCuWN25-7-4
GOST 5632 06Kh23N28
Tensile Strength
730-930 MPa
≥510 MPa
Yield Strength
>=530 MPa
≥196 MPa
Elongation
>=25%
≥35%
Hardness
<=290 HB
Not specified
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Not specified
Max Service Temp
Not specified
1050°C
Typical Applications
EN 10088-3 X2CrNiMoCuWN25-7-4
General purposes, semi-finished products, bars, rods, wire, sections and bright products
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
EN 10088-3 X2CrNiMoCuWN25-7-4 specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can EN 10088-3 X2CrNiMoCuWN25-7-4 Be Substituted With GOST 5632 06Kh23N28?
EN 10088-3 X2CrNiMoCuWN25-7-4 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-3 X2CrNiMoCuWN25-7-4 and GOST 5632 06Kh23N28?
EN 10088-3 X2CrNiMoCuWN25-7-4 specifies P, S, Mo, N which are not specified for GOST 5632 06Kh23N28.
Can EN 10088-3 X2CrNiMoCuWN25-7-4 be substituted with GOST 5632 06Kh23N28?
EN 10088-3 X2CrNiMoCuWN25-7-4 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.