EN 10088-3 X2CrNiMoN17-13-3 vs BS 970 (Part 3) 316S13
Strong Match — 90.7% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X2CrNiMoN17-13-3 (EN 10088-3:2014) and BS 970 (Part 3) 316S13 (BS 970 (Part 3):1991) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X2CrNiMoN17-13-3 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while BS 970 (Part 3) 316S13 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; austenitic stainless and heat resisting steel (table 18).
EN 10088-3 X2CrNiMoN17-13-3 is defined under European Standard (EN), originating from Europe, while BS 970 (Part 3) 316S13 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, EN 10088-3 X2CrNiMoN17-13-3 vs BS 970 (Part 3) 316S13 is a 90.7% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 90.7%.
Frequently Compared With EN 10088-3 X2CrNiMoN17-13-3:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X2CrNiMoN17-13-3
BS 970 (Part 3) 316S13
Tensile Strength
580-800 MPa
Not specified
Yield Strength
>=280 MPa
Not specified
Elongation
>=40%
Not specified
Hardness
<=250 HB
Not specified
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Not specified
Typical Applications
EN 10088-3 X2CrNiMoN17-13-3
General purposes, semi-finished products, bars, rods, wire, sections and bright products
BS 970 (Part 3) 316S13
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; austenitic stainless and heat resisting steel (Table 18)
Key Differences
EN 10088-3 X2CrNiMoN17-13-3 specifies N which is not specified for BS 970 (Part 3) 316S13.
Can EN 10088-3 X2CrNiMoN17-13-3 Be Substituted With BS 970 (Part 3) 316S13?
EN 10088-3 X2CrNiMoN17-13-3 and BS 970 (Part 3) 316S13 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 316S13 is often considered as a substitute for EN 10088-3 X2CrNiMoN17-13-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-3 X2CrNiMoN17-13-3 and BS 970 (Part 3) 316S13?
EN 10088-3 X2CrNiMoN17-13-3 specifies N which is not specified for BS 970 (Part 3) 316S13.
Can EN 10088-3 X2CrNiMoN17-13-3 be substituted with BS 970 (Part 3) 316S13?
EN 10088-3 X2CrNiMoN17-13-3 and BS 970 (Part 3) 316S13 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 3) 316S13 is often considered as a substitute for EN 10088-3 X2CrNiMoN17-13-3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.