Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
P
S
Cr
Ni
N
<=0.030
<=1.00
<=2.00
<=0.045
<=0.030
17.5-19.5
8.5-11.5
0.12-0.22
Mechanical Properties
Tensile Strength
550-760 MPa
Yield Strength
>=270 MPa
Elongation
>=40%
Hardness
<=230 HB
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
More data from EN 10088-3:2014
From the standard
Mechanical properties by thickness or diameter2 size ranges
Thickness or diameter (mm)
Hardness HBW, max (guidance)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
Rm (MPa)
A min, longitudinal (%)
A min, transverse (%)
KV2 min, longitudinal (J)
KV2 min, transverse (J)
up to 160
230
270
305
550 to 760
40
-
100
-
over 160 to 250
230
270
305
550 to 760
-
30
-
60
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D; for rods only the tensile strength values apply.
Source: EN 10088-3:2014, Table 8
Proof strength at elevated temperature10 temperatures
Temperature (deg C)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
100
205
240
150
175
210
200
157
187
250
145
175
300
136
167
350
130
160
400
125
156
450
121
152
500
119
149
550
118
147
Minimum values, solution annealed (+AT).
Source: EN 10088-3:2014, Table 20
Hot forming and solution annealingguideline temperatures
Hot forming temperature
1200 to 900 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1000 to 1100 deg C
Cooling after solution annealing
water, air
Informative guideline; cooling must be rapid enough to avoid intergranular corrosion.
Source: EN 10088-3:2014, Table A.1