EN 10088-3 X2CrNiN23-4 vs EN 10088-1 X2CrNiN22-2

Close Alternative — 76.8% match based on chemical composition and mechanical property overlap.

EN 10088-3 X2CrNiN23-4 (EN 10088-3:2014) and EN 10088-1 X2CrNiN22-2 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X2CrNiN23-4 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X2CrNiN22-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X2CrNiN23-4 vs EN 10088-1 X2CrNiN22-2 is a 76.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.8%.

Frequently Compared With EN 10088-3 X2CrNiN23-4:
EN 10088-1 1.4401 ASTM A959 2304 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
76.8%
MECHANICAL MATCH
No shared data
OVERALL
76.8%
Specifications
Property EN 10088-3 X2CrNiN23-4 EN 10088-1 X2CrNiN22-2
Standard EN 10088-3:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
P (%) <=0.035 <=0.040
S (%) <=0.015 <=0.010
Cr (%) 22.0-24.5 21.5-24.0
Mo (%) 0.10-0.60 <=0.45
Ni (%) 3.5-5.5 1.00-2.90
N (%) 0.05-0.20 0.16-0.28
Cu (%) 0.10-0.60 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X2CrNiN23-4 EN 10088-1 X2CrNiN22-2
Tensile Strength 600-830 MPa Not specified
Yield Strength >=400 MPa Not specified
Elongation >=25% Not specified
Hardness <=260 HB Not specified
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X2CrNiN23-4
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X2CrNiN22-2
Not documented
Key Differences
Can EN 10088-3 X2CrNiN23-4 Be Substituted With EN 10088-1 X2CrNiN22-2?
EN 10088-3 X2CrNiN23-4 and EN 10088-1 X2CrNiN22-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-3 X2CrNiN23-4
0 active listings and RFQs →
EN 10088-1 X2CrNiN22-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X2CrNiN23-4 and EN 10088-1 X2CrNiN22-2?
EN 10088-3 X2CrNiN23-4 specifies Cu which is not specified for EN 10088-1 X2CrNiN22-2.
Can EN 10088-3 X2CrNiN23-4 be substituted with EN 10088-1 X2CrNiN22-2?
EN 10088-3 X2CrNiN23-4 and EN 10088-1 X2CrNiN22-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.