EN 10088-3 X3CrMnNiCu15-8-5-3 vs EN 10088-1 X2CrNiN23-4

Related Material — 68.7% match based on chemical composition and mechanical property overlap.

EN 10088-3 X3CrMnNiCu15-8-5-3 (EN 10088-3:2014) and EN 10088-1 X2CrNiN23-4 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X3CrMnNiCu15-8-5-3 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X2CrNiN23-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X3CrMnNiCu15-8-5-3 vs EN 10088-1 X2CrNiN23-4 is a 68.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 68.7%.

Frequently Compared With EN 10088-3 X3CrMnNiCu15-8-5-3:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 2304 ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
68.7%
MECHANICAL MATCH
No shared data
OVERALL
68.7%
Specifications
Property EN 10088-3 X3CrMnNiCu15-8-5-3 EN 10088-1 X2CrNiN23-4
Standard EN 10088-3:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) 7.0-9.0 <=2.00
P (%) <=0.040 <=0.035
S (%) <=0.010 <=0.015
Cr (%) 14.0-16.0 22.0-24.5
Mo (%) <=0.80 0.10-0.60
Ni (%) 4.5-6.0 3.5-5.5
N (%) 0.02-0.06 0.05-0.20
Cu (%) 2.0-4.0 0.10-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X3CrMnNiCu15-8-5-3 EN 10088-1 X2CrNiN23-4
Tensile Strength 400-600 MPa Not specified
Yield Strength >=175 MPa Not specified
Elongation >=45% Not specified
Hardness <=180 HB Not specified
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X3CrMnNiCu15-8-5-3
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X2CrNiN23-4
Not documented
Can EN 10088-3 X3CrMnNiCu15-8-5-3 Be Substituted With EN 10088-1 X2CrNiN23-4?
EN 10088-3 X3CrMnNiCu15-8-5-3 and EN 10088-1 X2CrNiN23-4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-3 X3CrMnNiCu15-8-5-3
0 active listings and RFQs →
EN 10088-1 X2CrNiN23-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X3CrMnNiCu15-8-5-3 and EN 10088-1 X2CrNiN23-4?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-3 X3CrMnNiCu15-8-5-3 be substituted with EN 10088-1 X2CrNiN23-4?
EN 10088-3 X3CrMnNiCu15-8-5-3 and EN 10088-1 X2CrNiN23-4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.