EN 10088-3 X3CrNiCuMo17-11-3-2 vs GB/T 3280 06Cr19Ni10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-3 X3CrNiCuMo17-11-3-2 (EN 10088-3:2014) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X3CrNiCuMo17-11-3-2 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. EN 10088-3 X3CrNiCuMo17-11-3-2 is defined under European Standard (EN), originating from Europe, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, EN 10088-3 X3CrNiCuMo17-11-3-2 vs GB/T 3280 06Cr19Ni10 is a 66.7% match. As per mechanical properties, the match is 12%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-3 X3CrNiCuMo17-11-3-2:
GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH ASTM A959 .- GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
66.7%
MECHANICAL MATCH
12%
OVERALL
35%
Specifications
Property EN 10088-3 X3CrNiCuMo17-11-3-2 GB/T 3280 06Cr19Ni10
Standard EN 10088-3:2014 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.04 0.08 max
Si (%) <=1.00 1.00 max
Mn (%) <=2.00 2.00 max
P (%) <=0.045 0.045 max
S (%) <=0.015 0.030 max
Cr (%) 16.5-17.5 18.00-20.00
Mo (%) 2.00-2.50 Not specified
Ni (%) 10.0-11.0 8.00-11.00
N (%) <=0.10 Not specified
Cu (%) 3.0-3.5 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X3CrNiCuMo17-11-3-2 GB/T 3280 06Cr19Ni10
Tensile Strength 450-650 MPa 520-720 MPa
Yield Strength >=175 MPa 205-310 MPa
Elongation >=45% 40-60%
Hardness <=215 HB 187 HB max
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X3CrNiCuMo17-11-3-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can EN 10088-3 X3CrNiCuMo17-11-3-2 Be Substituted With GB/T 3280 06Cr19Ni10?
EN 10088-3 X3CrNiCuMo17-11-3-2 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-3 X3CrNiCuMo17-11-3-2
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
EN 10088-3 X3CrNiCuMo17-11-3-2
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X3CrNiCuMo17-11-3-2 and GB/T 3280 06Cr19Ni10?
EN 10088-3 X3CrNiCuMo17-11-3-2 specifies Mo, N, Cu which are not specified for GB/T 3280 06Cr19Ni10.
Can EN 10088-3 X3CrNiCuMo17-11-3-2 be substituted with GB/T 3280 06Cr19Ni10?
EN 10088-3 X3CrNiCuMo17-11-3-2 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.