EN 10088-3 X3CrNiMo13-4 vs ASTM A959 S41500

Close Alternative — 76.1% match based on chemical composition and mechanical property overlap.

EN 10088-3 X3CrNiMo13-4 (EN 10088-3:2014) and ASTM A959 S41500 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X3CrNiMo13-4 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while ASTM A959 S41500 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). EN 10088-3 X3CrNiMo13-4 is defined under European Standard (EN), originating from Europe, while ASTM A959 S41500 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-3 X3CrNiMo13-4 vs ASTM A959 S41500 is a 76.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.1%.

Frequently Compared With EN 10088-3 X3CrNiMo13-4:
ASTM A959 25-4-4 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
76.1%
MECHANICAL MATCH
No shared data
OVERALL
76.1%
Specifications
Property EN 10088-3 X3CrNiMo13-4 ASTM A959 S41500
Standard EN 10088-3:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.05 <=0.05
Si (%) <=0.70 <=0.60
Mn (%) <=1.50 0.50-1.00
P (%) <=0.040 <=0.030
S (%) <=0.015 <=0.030
Cr (%) 12.0-14.0 11.5-14.0
Mo (%) 0.30-0.70 0.50-1.00
Ni (%) 3.5-4.5 3.5-5.5
N (%) >=0.020 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X3CrNiMo13-4 ASTM A959 S41500
Tensile Strength <=1100 MPa Not specified
Hardness <=320 HB Not specified
Condition Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, size range not stated; hardness for guidance only Not specified
Typical Applications
EN 10088-3 X3CrNiMo13-4
General purposes, semi-finished products, bars, rods, wire, sections and bright products
ASTM A959 S41500
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can EN 10088-3 X3CrNiMo13-4 Be Substituted With ASTM A959 S41500?
EN 10088-3 X3CrNiMo13-4 and ASTM A959 S41500 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-3 X3CrNiMo13-4
0 active listings and RFQs →
ASTM A959 S41500
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X3CrNiMo13-4 and ASTM A959 S41500?
EN 10088-3 X3CrNiMo13-4 specifies N which is not specified for ASTM A959 S41500.
Can EN 10088-3 X3CrNiMo13-4 be substituted with ASTM A959 S41500?
EN 10088-3 X3CrNiMo13-4 and ASTM A959 S41500 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.