EN 10088-3 X3CrNiMo13-4 vs IS 6603 X03Cr13Ni4Mo

Strong Match — 91.4% match based on chemical composition and mechanical property overlap.

EN 10088-3 X3CrNiMo13-4 (EN 10088-3:2014) and IS 6603 X03Cr13Ni4Mo (IS 6603:2024) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X3CrNiMo13-4 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while IS 6603 X03Cr13Ni4Mo is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars. EN 10088-3 X3CrNiMo13-4 is defined under European Standard (EN), originating from Europe, while IS 6603 X03Cr13Ni4Mo is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-3 X3CrNiMo13-4 vs IS 6603 X03Cr13Ni4Mo is a 87.2% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 91.4%.

Frequently Compared With EN 10088-3 X3CrNiMo13-4:
ASTM A959 25-4-4 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
87.2%
MECHANICAL MATCH
100%
OVERALL
91.4%
Specifications
Property EN 10088-3 X3CrNiMo13-4 IS 6603 X03Cr13Ni4Mo
Standard EN 10088-3:2014 IS 6603:2024
Category Stainless Steel Stainless Steel
C (%) <=0.05 <=0.05
Si (%) <=0.70 <=0.70
Mn (%) <=1.50 0.50-1.00
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.015
Cr (%) 12.0-14.0 12.0-14.0
Mo (%) 0.30-0.70 0.30-1.00
Ni (%) 3.5-4.5 3.5-4.5
N (%) >=0.020 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X3CrNiMo13-4 IS 6603 X03Cr13Ni4Mo
Tensile Strength <=1100 MPa <=1100 MPa
Hardness <=320 HB <=320 HB
Condition Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, size range not stated; hardness for guidance only Soft annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, all sizes; hardness as printed
Typical Applications
EN 10088-3 X3CrNiMo13-4
General purposes, semi-finished products, bars, rods, wire, sections and bright products
IS 6603 X03Cr13Ni4Mo
General purposes, semi-finished products, bars, wire rods and bright bars
Key Differences
Can EN 10088-3 X3CrNiMo13-4 Be Substituted With IS 6603 X03Cr13Ni4Mo?
EN 10088-3 X3CrNiMo13-4 and IS 6603 X03Cr13Ni4Mo overlap closely enough on chemistry and mechanical properties that IS 6603 X03Cr13Ni4Mo is often considered as a substitute for EN 10088-3 X3CrNiMo13-4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-3 X3CrNiMo13-4
0 active listings and RFQs →
IS 6603 X03Cr13Ni4Mo
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X3CrNiMo13-4 and IS 6603 X03Cr13Ni4Mo?
EN 10088-3 X3CrNiMo13-4 specifies N which is not specified for IS 6603 X03Cr13Ni4Mo.
Can EN 10088-3 X3CrNiMo13-4 be substituted with IS 6603 X03Cr13Ni4Mo?
EN 10088-3 X3CrNiMo13-4 and IS 6603 X03Cr13Ni4Mo overlap closely enough on chemistry and mechanical properties that IS 6603 X03Cr13Ni4Mo is often considered as a substitute for EN 10088-3 X3CrNiMo13-4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.