Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
P
S
Cr
0.43-0.50
<=1.00
<=2.00
<=0.040
0.15-0.35
12.5-14.0
Mechanical Properties
Tensile Strength
<=800 MPa
Hardness
<=245 HB
Condition
Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 63 mm; hardness for guidance only
More data from EN 10088-3:2014
From the standard
Mechanical properties by heat treatment condition1 rows
Thickness or diameter (mm)
Condition
Hardness HBW, max (guidance)
Rp0.2 min (MPa)
Rm (MPa)
A min, longitudinal (%)
A min, transverse (%)
KV2 min, longitudinal (J)
KV2 min, transverse (J)
up to 63
+A
245
-
max. 800
-
-
-
-
+A = annealed, +QT = quenched and tempered; for rods only the tensile strength values apply.
Source: EN 10088-3:2014, Table 11
Bright bars, annealed and quenched and tempered4 size ranges
Thickness or diameter (mm)
Annealed Rm max (MPa)
Annealed HB max (information)
Quenched and tempered Rp0.2 min (MPa)
Quenched and tempered Rm (MPa)
A5 min, longitudinal (%)
A5 min, transverse (%)
KV2 min, longitudinal (J)
KV2 min, transverse (J)
up to 10
880
280
-
-
-
-
-
-
over 10 to 16
880
280
-
-
-
-
-
-
over 16 to 40
800
250
-
-
-
-
-
-
over 40 to 63
760
230
-
-
-
-
-
-
Bright bars, conditions 2H, 2B, 2G or 2P; no quenched and tempered values given.
Source: EN 10088-3:2014, Table 16
Hot forming and heat treatment1 conditions
Condition
Annealing temperature (deg C)
Cooling after annealing
Quenching temperature (deg C)
Quenching medium
Tempering temperature (deg C)
+A
750 to 850
-
-
-
-
Hot forming 1100 to 800 deg C, cooling: slow cooling. Informative guideline.
Source: EN 10088-3:2014, Table A.4
Active EN 10088-3:2014 X46CrS13 Listings on M-EX (For Sale)