EN 10088-3 X5CrNiCuNb16-4 vs IS 6603 X05Cr16Ni4CuNb
Close Alternative — 83.3% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X5CrNiCuNb16-4 (EN 10088-3:2014) and IS 6603 X05Cr16Ni4CuNb (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X5CrNiCuNb16-4 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while IS 6603 X05Cr16Ni4CuNb is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
EN 10088-3 X5CrNiCuNb16-4 is defined under European Standard (EN), originating from Europe, while IS 6603 X05Cr16Ni4CuNb is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-3 X5CrNiCuNb16-4 vs IS 6603 X05Cr16Ni4CuNb is a 100% match.
As per mechanical properties, the match is 50%.
Combined, this makes them a close alternative overall at 83.3%.
Frequently Compared With EN 10088-3 X5CrNiCuNb16-4:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X5CrNiCuNb16-4
IS 6603 X05Cr16Ni4CuNb
Tensile Strength
<=1200 MPa
<=1200 MPa
Hardness
<=360 HB
<=363 HB
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 100 mm; hardness for guidance only
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D; hardness as printed
Typical Applications
EN 10088-3 X5CrNiCuNb16-4
General purposes, semi-finished products, bars, rods, wire, sections and bright products
IS 6603 X05Cr16Ni4CuNb
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-3 X5CrNiCuNb16-4 Be Substituted With IS 6603 X05Cr16Ni4CuNb?
EN 10088-3 X5CrNiCuNb16-4 and IS 6603 X05Cr16Ni4CuNb are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10088-3 X5CrNiCuNb16-4 and IS 6603 X05Cr16Ni4CuNb?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-3 X5CrNiCuNb16-4 be substituted with IS 6603 X05Cr16Ni4CuNb?
EN 10088-3 X5CrNiCuNb16-4 and IS 6603 X05Cr16Ni4CuNb are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.