Related Material — 66.8% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X5CrNiN19-9 (EN 10088-3:2014) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X5CrNiN19-9 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners..
EN 10088-3 X5CrNiN19-9 is defined under European Standard (EN), originating from Europe, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.
As per chemical composition, EN 10088-3 X5CrNiN19-9 vs GB/T 3280 06Cr19Ni10 is a 91% match.
As per mechanical properties, the match is 18.5%.
Combined, this makes them a related material overall at 66.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X5CrNiN19-9
GB/T 3280 06Cr19Ni10
Tensile Strength
550-750 MPa
520-720 MPa
Yield Strength
>=270 MPa
205-310 MPa
Elongation
>=40%
40-60%
Hardness
<=215 HB
187 HB max
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 40 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Not specified
Typical Applications
EN 10088-3 X5CrNiN19-9
General purposes, semi-finished products, bars, rods, wire, sections and bright products
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
EN 10088-3 X5CrNiN19-9 specifies N which is not specified for GB/T 3280 06Cr19Ni10.
Can EN 10088-3 X5CrNiN19-9 Be Substituted With GB/T 3280 06Cr19Ni10?
EN 10088-3 X5CrNiN19-9 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-3 X5CrNiN19-9 and GB/T 3280 06Cr19Ni10?
EN 10088-3 X5CrNiN19-9 specifies N which is not specified for GB/T 3280 06Cr19Ni10.
Can EN 10088-3 X5CrNiN19-9 be substituted with GB/T 3280 06Cr19Ni10?
EN 10088-3 X5CrNiN19-9 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.