EN 10088-3 X5NiCrTiMoVB25-15-2 vs ASTM A959 622

Related Material — 65.9% match based on chemical composition and mechanical property overlap.

EN 10088-3 X5NiCrTiMoVB25-15-2 (EN 10088-3:2014) and ASTM A959 622 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X5NiCrTiMoVB25-15-2 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while ASTM A959 622 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). EN 10088-3 X5NiCrTiMoVB25-15-2 is defined under European Standard (EN), originating from Europe, while ASTM A959 622 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-3 X5NiCrTiMoVB25-15-2 vs ASTM A959 622 is a 65.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65.9%.

Frequently Compared With EN 10088-3 X5NiCrTiMoVB25-15-2:
ASTM A959 .- GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
65.9%
MECHANICAL MATCH
No shared data
OVERALL
65.9%
Specifications
Property EN 10088-3 X5NiCrTiMoVB25-15-2 ASTM A959 622
Standard EN 10088-3:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.00 <=1.00
Mn (%) 1.00-2.00 <=1.50
P (%) <=0.025 <=0.040
S (%) <=0.015 <=0.030
Cr (%) 13.0-16.0 12.0-15.0
Mo (%) 1.00-1.50 2.5-3.5
Ni (%) 24.0-27.0 24.0-28.0
B (%) 0.0010-0.010 0.001-0.010
Al (%) <=0.35 <=0.35
Ti (%) 1.90-2.30 1.55-2.00
V (%) 0.10-0.50 Not specified
Cu (%) Not specified <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X5NiCrTiMoVB25-15-2 ASTM A959 622
Tensile Strength <=700 MPa Not specified
Yield Strength >=250 MPa Not specified
Elongation >=35% Not specified
Hardness <=212 HB Not specified
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 50 mm; hardness for guidance only Not specified
Typical Applications
EN 10088-3 X5NiCrTiMoVB25-15-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
ASTM A959 622
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can EN 10088-3 X5NiCrTiMoVB25-15-2 Be Substituted With ASTM A959 622?
EN 10088-3 X5NiCrTiMoVB25-15-2 and ASTM A959 622 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-3 X5NiCrTiMoVB25-15-2
0 active listings and RFQs →
ASTM A959 622
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X5NiCrTiMoVB25-15-2 and ASTM A959 622?
EN 10088-3 X5NiCrTiMoVB25-15-2 specifies V which is not specified for ASTM A959 622. ASTM A959 622 specifies Cu which is not specified for EN 10088-3 X5NiCrTiMoVB25-15-2.
Can EN 10088-3 X5NiCrTiMoVB25-15-2 be substituted with ASTM A959 622?
EN 10088-3 X5NiCrTiMoVB25-15-2 and ASTM A959 622 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.