EN 10088-3 X6CrMnNiCuN18-12-4-2 vs EN 10088-1 1.4845
Minimal Match — 32.6% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X6CrMnNiCuN18-12-4-2 (EN 10088-3:2014) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X6CrMnNiCuN18-12-4-2 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components.
EN 10088-3 X6CrMnNiCuN18-12-4-2 is defined under European Standard (EN), originating from Europe, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10088-3 X6CrMnNiCuN18-12-4-2 vs EN 10088-1 1.4845 is a 48.9% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 32.6%.
Frequently Compared With EN 10088-3 X6CrMnNiCuN18-12-4-2:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X6CrMnNiCuN18-12-4-2
EN 10088-1 1.4845
Tensile Strength
650-850 MPa
≥515 MPa
Yield Strength
>=380 MPa
≥205 MPa
Elongation
>=30%
≥40%
Hardness
<=260 HB
Not specified
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 8 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Not specified
Max Service Temp
Not specified
1100°C continuous
Typical Applications
EN 10088-3 X6CrMnNiCuN18-12-4-2
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
EN 10088-3 X6CrMnNiCuN18-12-4-2 specifies P, S, Mo, N which are not specified for EN 10088-1 1.4845.
Can EN 10088-3 X6CrMnNiCuN18-12-4-2 Be Substituted With EN 10088-1 1.4845?
EN 10088-3 X6CrMnNiCuN18-12-4-2 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-3 X6CrMnNiCuN18-12-4-2 and EN 10088-1 1.4845?
EN 10088-3 X6CrMnNiCuN18-12-4-2 specifies P, S, Mo, N which are not specified for EN 10088-1 1.4845.
Can EN 10088-3 X6CrMnNiCuN18-12-4-2 be substituted with EN 10088-1 1.4845?
EN 10088-3 X6CrMnNiCuN18-12-4-2 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.