EN 10088-3 X6CrNiTi18-10 vs EN 10088-1 X6CrNiNb18-10
Strong Match — 93.5% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X6CrNiTi18-10 (EN 10088-3:2014) and EN 10088-1 X6CrNiNb18-10 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X6CrNiTi18-10 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X6CrNiNb18-10 is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10088-3 X6CrNiTi18-10 vs EN 10088-1 X6CrNiNb18-10 is a 93.5% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 93.5%.
Frequently Compared With EN 10088-3 X6CrNiTi18-10:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X6CrNiTi18-10
EN 10088-1 X6CrNiNb18-10
Tensile Strength
500-700 MPa
Not specified
Yield Strength
>=190 MPa
Not specified
Elongation
>=40%
Not specified
Hardness
<=215 HB
Not specified
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Not specified
Typical Applications
EN 10088-3 X6CrNiTi18-10
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X6CrNiNb18-10
Not documented
Key Differences
EN 10088-3 X6CrNiTi18-10 specifies Ti which is not specified for EN 10088-1 X6CrNiNb18-10.
Can EN 10088-3 X6CrNiTi18-10 Be Substituted With EN 10088-1 X6CrNiNb18-10?
EN 10088-3 X6CrNiTi18-10 and EN 10088-1 X6CrNiNb18-10 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X6CrNiNb18-10 is often considered as a substitute for EN 10088-3 X6CrNiTi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-3 X6CrNiTi18-10 and EN 10088-1 X6CrNiNb18-10?
EN 10088-3 X6CrNiTi18-10 specifies Ti which is not specified for EN 10088-1 X6CrNiNb18-10.
Can EN 10088-3 X6CrNiTi18-10 be substituted with EN 10088-1 X6CrNiNb18-10?
EN 10088-3 X6CrNiTi18-10 and EN 10088-1 X6CrNiNb18-10 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X6CrNiNb18-10 is often considered as a substitute for EN 10088-3 X6CrNiTi18-10 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.