EN 10088-3 X8CrMnCuN17-8-3 vs EN 10088-1 X10CrNi18-8

Related Material — 65.8% match based on chemical composition and mechanical property overlap.

EN 10088-3 X8CrMnCuN17-8-3 (EN 10088-3:2014) and EN 10088-1 X10CrNi18-8 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X8CrMnCuN17-8-3 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X10CrNi18-8 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X8CrMnCuN17-8-3 vs EN 10088-1 X10CrNi18-8 is a 65.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65.8%.

Frequently Compared With EN 10088-3 X8CrMnCuN17-8-3:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
65.8%
MECHANICAL MATCH
No shared data
OVERALL
65.8%
Specifications
Property EN 10088-3 X8CrMnCuN17-8-3 EN 10088-1 X10CrNi18-8
Standard EN 10088-3:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.10 0.030-0.15
Si (%) <=2.00 <=2.00
Mn (%) 6.5-9.0 <=2.00
P (%) <=0.040 <=0.045
S (%) <=0.030 <=0.015
Cr (%) 15.0-18.0 16.0-19.0
Mo (%) <=1.00 <=0.80
Ni (%) <=3.00 6.0-9.5
N (%) 0.10-0.30 <=0.10
Cu (%) 2.00-3.5 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X8CrMnCuN17-8-3 EN 10088-1 X10CrNi18-8
Tensile Strength 560-780 MPa Not specified
Yield Strength >=270 MPa Not specified
Elongation >=40% Not specified
Hardness <=245 HB Not specified
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X8CrMnCuN17-8-3
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X10CrNi18-8
Not documented
Key Differences
Can EN 10088-3 X8CrMnCuN17-8-3 Be Substituted With EN 10088-1 X10CrNi18-8?
EN 10088-3 X8CrMnCuN17-8-3 and EN 10088-1 X10CrNi18-8 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-3 X8CrMnCuN17-8-3
0 active listings and RFQs →
EN 10088-1 X10CrNi18-8
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X8CrMnCuN17-8-3 and EN 10088-1 X10CrNi18-8?
EN 10088-3 X8CrMnCuN17-8-3 specifies Cu which is not specified for EN 10088-1 X10CrNi18-8.
Can EN 10088-3 X8CrMnCuN17-8-3 be substituted with EN 10088-1 X10CrNi18-8?
EN 10088-3 X8CrMnCuN17-8-3 and EN 10088-1 X10CrNi18-8 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.