EN 10088-3 X8CrMnNiN18-9-5 vs EN 10088-1 X6CrNiMnCuN18-12-4-2

Related Material — 66.7% match based on chemical composition and mechanical property overlap.

EN 10088-3 X8CrMnNiN18-9-5 (EN 10088-3:2014) and EN 10088-1 X6CrNiMnCuN18-12-4-2 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-3 X8CrMnNiN18-9-5 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X6CrNiMnCuN18-12-4-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-3 X8CrMnNiN18-9-5 vs EN 10088-1 X6CrNiMnCuN18-12-4-2 is a 66.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 66.7%.

Frequently Compared With EN 10088-3 X8CrMnNiN18-9-5:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
66.7%
MECHANICAL MATCH
No shared data
OVERALL
66.7%
Specifications
Property EN 10088-3 X8CrMnNiN18-9-5 EN 10088-1 X6CrNiMnCuN18-12-4-2
Standard EN 10088-3:2014 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.05-0.10 0.02-0.10
Si (%) 0.30-0.60 <=1.00
Mn (%) 9.0-10.0 10.5-12.5
P (%) <=0.035 <=0.050
S (%) <=0.030 <=0.015
Cr (%) 17.5-18.5 17.0-19.0
Mo (%) <=0.50 <=0.50
Ni (%) 5.0-6.0 3.5-4.5
N (%) 0.25-0.32 0.20-0.30
Cu (%) <=0.40 1.50-3.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-3 X8CrMnNiN18-9-5 EN 10088-1 X6CrNiMnCuN18-12-4-2
Tensile Strength 700-900 MPa Not specified
Yield Strength >=350 MPa Not specified
Elongation >=35% Not specified
Hardness <=260 HB Not specified
Condition Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 10 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only Not specified
Typical Applications
EN 10088-3 X8CrMnNiN18-9-5
General purposes, semi-finished products, bars, rods, wire, sections and bright products
EN 10088-1 X6CrNiMnCuN18-12-4-2
Not documented
Can EN 10088-3 X8CrMnNiN18-9-5 Be Substituted With EN 10088-1 X6CrNiMnCuN18-12-4-2?
EN 10088-3 X8CrMnNiN18-9-5 and EN 10088-1 X6CrNiMnCuN18-12-4-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-3 X8CrMnNiN18-9-5
0 active listings and RFQs →
EN 10088-1 X6CrNiMnCuN18-12-4-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-3 X8CrMnNiN18-9-5 and EN 10088-1 X6CrNiMnCuN18-12-4-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-3 X8CrMnNiN18-9-5 be substituted with EN 10088-1 X6CrNiMnCuN18-12-4-2?
EN 10088-3 X8CrMnNiN18-9-5 and EN 10088-1 X6CrNiMnCuN18-12-4-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.