EN ISO 683-17 100Cr6 vs IS 1570 (Part 6) T105Cr5

Strong Match — 85.3% match based on chemical composition and mechanical property overlap.

EN ISO 683-17 100Cr6 (EN ISO 683-17:2014) and IS 1570 (Part 6) T105Cr5 (IS 1570 (Part 6):1996) are both steel grades. Both fall under the Tool & Die Steels category. EN ISO 683-17 100Cr6 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 6) T105Cr5 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN ISO 683-17 100Cr6 vs IS 1570 (Part 6) T105Cr5 is a 85.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 85.3%.

Frequently Compared With EN ISO 683-17 100Cr6:
AISI 52100 GB/T 1299 4Cr5MoSiV EN ISO 4957 1.2316 DIN EN ISO 4957 1.2379 GOST 5950 4H5MFS DIN EN ISO 4957 1.2344 GB/T 1299 4Cr5MoSiV1 GB/T 1299 3Cr2W8V GOST 5950 3H2W8F GOST 5950 4H5MFS1 IS 1570 (Part 6) 133T3 IS 1570 (Part 6) 55T8
Match Breakdown
CHEMISTRY MATCH
85.3%
MECHANICAL MATCH
No shared data
OVERALL
85.3%
Specifications
Property EN ISO 683-17 100Cr6 IS 1570 (Part 6) T105Cr5
Standard EN ISO 683-17:2014 IS 1570 (Part 6):1996
Category Tool & Die Steels Tool & Die Steels
C (%) 0.93–1.05 0.90-1.20
Si (%) 0.15–0.35 0.10-0.35
Mn (%) 0.25–0.45 0.20-0.40
Cr (%) 1.35–1.65 1.00-1.60
S (%) ≤0.025 <=0.035
P (%) ≤0.025 <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN ISO 683-17 100Cr6 IS 1570 (Part 6) T105Cr5
Tensile Strength ≥620 MPa (annealed) Not specified
Hardness HRC 60–66 (hardened) Not specified
Hardness HB 179–217 (annealed) Not specified
Typical Applications
EN ISO 683-17 100Cr6
Rolling element bearings, precision components, cold work tooling
IS 1570 (Part 6) T105Cr5
Not documented
Can EN ISO 683-17 100Cr6 Be Substituted With IS 1570 (Part 6) T105Cr5?
EN ISO 683-17 100Cr6 and IS 1570 (Part 6) T105Cr5 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 6) T105Cr5 is often considered as a substitute for EN ISO 683-17 100Cr6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
EN ISO 683-17 100Cr6
Round Bar → (18 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 3000–6500 mm (118.11–255.91 in)
IS 1570 (Part 6) T105Cr5
No active listings currently.
On M-EX Right Now
EN ISO 683-17 100Cr6
18 active listings and RFQs →
IS 1570 (Part 6) T105Cr5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN ISO 683-17 100Cr6 and IS 1570 (Part 6) T105Cr5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN ISO 683-17 100Cr6 be substituted with IS 1570 (Part 6) T105Cr5?
EN ISO 683-17 100Cr6 and IS 1570 (Part 6) T105Cr5 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 6) T105Cr5 is often considered as a substitute for EN ISO 683-17 100Cr6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.