GB/T 1591 Q390C vs CSA G40.21 400W

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

GB/T 1591 Q390C (GB/T 1591:2018) and CSA G40.21 400W (CSA G40.21-13 (R2023)) are both steel grades. Both fall under the Structural Steel category. GB/T 1591 Q390C is typically used for general structure for engineering (plates, strips, bars and sections), while CSA G40.21 400W is commonly used for heavy structural fabrication, bridges, offshore platforms, cranes, pressure vessels, mining equipment.. GB/T 1591 Q390C is defined under Guobiao Standards (GB/T), originating from China, while CSA G40.21 400W is defined under Canadian Standards Association (CSA), originating from Canada.

As per chemical composition, GB/T 1591 Q390C vs CSA G40.21 400W is a 70.1% match. As per mechanical properties, the match is 32.5%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GB/T 1591 Q390C:
CSA G40.21 480W
Other Structural Steel Grades to Compare With GB/T 1591 Q390C:
GOST 19281 09G2S CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 400A ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80 ASTM A283C ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
70.1%
MECHANICAL MATCH
32.5%
OVERALL
35%
Specifications
Property GB/T 1591 Q390C CSA G40.21 400W
Standard GB/T 1591:2018 CSA G40.21-13 (R2023)
Category Structural Steel Structural Steel
C (%) <=0.20 max 0.23
Si (%) <=0.55 max 0.5
Mn (%) <=1.70 max 1.6
P (%) <=0.030 max 0.035
S (%) <=0.030 max 0.035
Nb (%) <=0.05 Not specified
V (%) <=0.13 Not specified
Ti (%) <=0.05 Not specified
Cr (%) <=0.30 Not specified
Ni (%) <=0.50 Not specified
Cu (%) <=0.40 Not specified
Mo (%) <=0.10 Not specified
N (%) <=0.015 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 1591 Q390C CSA G40.21 400W
Tensile Strength 490-650 MPa 520-690 MPa
Yield Strength >=390 MPa 400 MPa min
Elongation >=21% Not specified
Condition Hot-rolled (as-rolled), nominal thickness or diameter up to 16 mm for yield; tensile strength for up to 100 mm; elongation longitudinal, up to 40 mm Not specified
Typical Applications
GB/T 1591 Q390C
General structure for engineering (plates, strips, bars and sections)
CSA G40.21 400W
Heavy structural fabrication, bridges, offshore platforms, cranes, pressure vessels, mining equipment.
Key Differences
Can GB/T 1591 Q390C Be Substituted With CSA G40.21 400W?
GB/T 1591 Q390C and CSA G40.21 400W share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GB/T 1591 Q390C
No active listings currently.
CSA G40.21 400W
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2500–5200 mm (98.43–204.72 in)
On M-EX Right Now
GB/T 1591 Q390C
0 active listings and RFQs →
CSA G40.21 400W
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 1591 Q390C and CSA G40.21 400W?
GB/T 1591 Q390C specifies Nb, V, Ti, Cr which are not specified for CSA G40.21 400W.
Can GB/T 1591 Q390C be substituted with CSA G40.21 400W?
GB/T 1591 Q390C and CSA G40.21 400W share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.