GB/T 1591 Q460C vs AS/NZS 3679.1 350

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

GB/T 1591 Q460C (GB/T 1591:2018) and AS/NZS 3679.1 350 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. GB/T 1591 Q460C is typically used for general structure for engineering (plates, strips, bars and sections), while AS/NZS 3679.1 350 is commonly used for hot-rolled structural bars and sections for primary structural beams, columns, and framing. GB/T 1591 Q460C is defined under Guobiao Standards (GB/T), originating from China, while AS/NZS 3679.1 350 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, GB/T 1591 Q460C vs AS/NZS 3679.1 350 is a 62.1% match. As per mechanical properties, the match is 18.8%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GB/T 1591 Q460C:
CSA G40.21 260W CSA G40.21 350W ASTM A1008 SS Grade 80 GOST 19281 09G2S CSA G40.21 300W CSA G40.21 400W CSA G40.21 480W ASTM A572 Gr.65
Other Structural Steel Grades to Compare With GB/T 1591 Q460C:
AS/NZS 3679.1 300 CSA G40.21 400A ASTM A1008 SS Grade 50 ASTM A283C
Match Breakdown
CHEMISTRY MATCH
62.1%
MECHANICAL MATCH
18.8%
OVERALL
35%
Specifications
Property GB/T 1591 Q460C AS/NZS 3679.1 350
Standard GB/T 1591:2018 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
C (%) <=0.20 <=0.22
Si (%) <=0.55 <=0.50
Mn (%) <=1.80 <=1.70
P (%) <=0.030 <=0.040
S (%) <=0.030 <=0.040
Nb (%) <=0.05 Not specified
V (%) <=0.13 Not specified
Ti (%) <=0.05 Not specified
Cr (%) <=0.30 Not specified
Ni (%) <=0.80 Not specified
Cu (%) <=0.40 Not specified
Mo (%) <=0.20 Not specified
N (%) <=0.015 Not specified
B (%) <=0.004 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 1591 Q460C AS/NZS 3679.1 350
Tensile Strength 550-720 MPa 480-640 MPa
Yield Strength >=460 MPa 350 MPa min
Condition Hot-rolled (as-rolled), nominal thickness or diameter up to 16 mm for yield; tensile strength for up to 100 mm Not specified
Elongation Not specified 20% min
Typical Applications
GB/T 1591 Q460C
General structure for engineering (plates, strips, bars and sections)
AS/NZS 3679.1 350
Hot-rolled structural bars and sections for primary structural beams, columns, and framing
Key Differences
Can GB/T 1591 Q460C Be Substituted With AS/NZS 3679.1 350?
GB/T 1591 Q460C and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GB/T 1591 Q460C
No active listings currently.
AS/NZS 3679.1 350
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3200 mm (114.17–125.98 in)
On M-EX Right Now
GB/T 1591 Q460C
0 active listings and RFQs →
AS/NZS 3679.1 350
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 1591 Q460C and AS/NZS 3679.1 350?
GB/T 1591 Q460C specifies Nb, V, Ti, Cr which are not specified for AS/NZS 3679.1 350.
Can GB/T 1591 Q460C be substituted with AS/NZS 3679.1 350?
GB/T 1591 Q460C and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.