GB/T 3077 18Cr2Ni4W vs GB/T 3077 37CrNi3

Related Material — 65.6% match based on chemical composition and mechanical property overlap.

GB/T 3077 18Cr2Ni4W (GB/T 3077:2015) and GB/T 3077 37CrNi3 (GB/T 3077:2015) are both steel grades. Both fall under the Alloy Steel category. GB/T 3077 18Cr2Ni4W is typically used for hot-rolled or forged structural alloy steel bars, while GB/T 3077 37CrNi3 is commonly used for hot-rolled or forged structural alloy steel bars. GB/T 3077 18Cr2Ni4W is defined under Guobiao Standards (GB/T), originating from China, while GB/T 3077 37CrNi3 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, GB/T 3077 18Cr2Ni4W vs GB/T 3077 37CrNi3 is a 73.3% match. As per mechanical properties, the match is 50%. Combined, this makes them a related material overall at 65.6%.

Frequently Compared With GB/T 3077 18Cr2Ni4W:
GB/T 3077 12Cr2Ni4 IS 4367 07Cr4Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
73.3%
MECHANICAL MATCH
50%
OVERALL
65.6%
Specifications
Property GB/T 3077 18Cr2Ni4W GB/T 3077 37CrNi3
Standard GB/T 3077:2015 GB/T 3077:2015
Category Alloy Steel Alloy Steel
C (%) 0.13-0.19 0.34-0.41
Si (%) 0.17-0.37 0.17-0.37
Mn (%) 0.30-0.60 0.30-0.60
Cr (%) 1.35-1.65 1.20-1.60
Ni (%) 4.00-4.50 3.00-3.50
W (%) 0.80-1.20 Not specified
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.030
Cu (%) <=0.30 <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3077 18Cr2Ni4W GB/T 3077 37CrNi3
Tensile Strength >=1180 MPa >=1130 MPa
Yield Strength >=835 MPa >=980 MPa
Elongation >=10% >=10%
Hardness <=269 HB <=269 HB
Condition Quenched and tempered, test sample 15 mm; hardness is for bars delivered annealed or high temperature tempered Quenched and tempered, test sample 25 mm; hardness is for bars delivered annealed or high temperature tempered
Typical Applications
GB/T 3077 18Cr2Ni4W
Hot-rolled or forged structural alloy steel bars
GB/T 3077 37CrNi3
Hot-rolled or forged structural alloy steel bars
Key Differences
Can GB/T 3077 18Cr2Ni4W Be Substituted With GB/T 3077 37CrNi3?
GB/T 3077 18Cr2Ni4W and GB/T 3077 37CrNi3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
GB/T 3077 18Cr2Ni4W
0 active listings and RFQs →
GB/T 3077 37CrNi3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3077 18Cr2Ni4W and GB/T 3077 37CrNi3?
GB/T 3077 18Cr2Ni4W specifies W which is not specified for GB/T 3077 37CrNi3.
Can GB/T 3077 18Cr2Ni4W be substituted with GB/T 3077 37CrNi3?
GB/T 3077 18Cr2Ni4W and GB/T 3077 37CrNi3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.