GB/T 3077 20Cr2Ni4 vs GB/T 3077 18Cr2Ni4W

Close Alternative — 76.1% match based on chemical composition and mechanical property overlap.

GB/T 3077 20Cr2Ni4 (GB/T 3077:2015) and GB/T 3077 18Cr2Ni4W (GB/T 3077:2015) are both steel grades. Both fall under the Alloy Steel category. GB/T 3077 20Cr2Ni4 is typically used for hot-rolled or forged structural alloy steel bars, while GB/T 3077 18Cr2Ni4W is commonly used for hot-rolled or forged structural alloy steel bars. GB/T 3077 20Cr2Ni4 is defined under Guobiao Standards (GB/T), originating from China, while GB/T 3077 18Cr2Ni4W is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, GB/T 3077 20Cr2Ni4 vs GB/T 3077 18Cr2Ni4W is a 76.7% match. As per mechanical properties, the match is 75%. Combined, this makes them a close alternative overall at 76.1%.

Frequently Compared With GB/T 3077 20Cr2Ni4:
GB/T 3077 12Cr2Ni4 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
76.7%
MECHANICAL MATCH
75%
OVERALL
76.1%
Specifications
Property GB/T 3077 20Cr2Ni4 GB/T 3077 18Cr2Ni4W
Standard GB/T 3077:2015 GB/T 3077:2015
Category Alloy Steel Alloy Steel
C (%) 0.17-0.23 0.13-0.19
Si (%) 0.17-0.37 0.17-0.37
Mn (%) 0.30-0.60 0.30-0.60
Cr (%) 1.25-1.65 1.35-1.65
Ni (%) 3.25-3.65 4.00-4.50
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.030
Cu (%) <=0.30 <=0.30
W (%) Not specified 0.80-1.20
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3077 20Cr2Ni4 GB/T 3077 18Cr2Ni4W
Tensile Strength >=1180 MPa >=1180 MPa
Yield Strength >=1080 MPa >=835 MPa
Elongation >=10% >=10%
Hardness <=269 HB <=269 HB
Condition Quenched and tempered, test sample 15 mm; hardness is for bars delivered annealed or high temperature tempered Quenched and tempered, test sample 15 mm; hardness is for bars delivered annealed or high temperature tempered
Typical Applications
GB/T 3077 20Cr2Ni4
Hot-rolled or forged structural alloy steel bars
GB/T 3077 18Cr2Ni4W
Hot-rolled or forged structural alloy steel bars
Key Differences
Can GB/T 3077 20Cr2Ni4 Be Substituted With GB/T 3077 18Cr2Ni4W?
GB/T 3077 20Cr2Ni4 and GB/T 3077 18Cr2Ni4W are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
GB/T 3077 20Cr2Ni4
0 active listings and RFQs →
GB/T 3077 18Cr2Ni4W
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3077 20Cr2Ni4 and GB/T 3077 18Cr2Ni4W?
GB/T 3077 18Cr2Ni4W specifies W which is not specified for GB/T 3077 20Cr2Ni4.
Can GB/T 3077 20Cr2Ni4 be substituted with GB/T 3077 18Cr2Ni4W?
GB/T 3077 20Cr2Ni4 and GB/T 3077 18Cr2Ni4W are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.