GB/T 3077 20CrMnMo vs IS 1570 (Part 7) 10Cr36Mo10H

Minimal Match — 40.4% match based on chemical composition and mechanical property overlap.

GB/T 3077 20CrMnMo (GB/T 3077:2015) and IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Alloy Steel category. GB/T 3077 20CrMnMo is typically used for hot-rolled or forged structural alloy steel bars, while IS 1570 (Part 7) 10Cr36Mo10H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. GB/T 3077 20CrMnMo is defined under Guobiao Standards (GB/T), originating from China, while IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, GB/T 3077 20CrMnMo vs IS 1570 (Part 7) 10Cr36Mo10H is a 60.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 40.4%.

Frequently Compared With GB/T 3077 20CrMnMo:
IS 1570 (Part 7) 10Mo6H UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 105Cr5 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
60.6%
MECHANICAL MATCH
0%
OVERALL
40.4%
Specifications
Property GB/T 3077 20CrMnMo IS 1570 (Part 7) 10Cr36Mo10H
Standard GB/T 3077:2015 IS 1570 (Part 7):1992
Category Alloy Steel Alloy Steel
C (%) 0.17-0.23 <=0.15
Si (%) 0.17-0.37 0.25-1.0
Mn (%) 0.90-1.20 0.30-0.60
Cr (%) 1.10-1.40 8.00-10.00
Mo (%) 0.20-0.30 0.90-1.10
P (%) <=0.030 <=0.040
S (%) <=0.030 <=0.030
Cu (%) <=0.30 Not specified
Al (metallic) (%) Not specified <=0.02
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3077 20CrMnMo IS 1570 (Part 7) 10Cr36Mo10H
Tensile Strength >=1180 MPa 410-560 MPa
Yield Strength >=885 MPa >=135 MPa (0.2 % proof stress)
Elongation >=10% >=20%
Hardness <=217 HB Not specified
Condition Quenched and tempered, test sample 15 mm; hardness is for bars delivered annealed or high temperature tempered Pipes, A, thickness - (first row of Table 3)
Typical Applications
GB/T 3077 20CrMnMo
Hot-rolled or forged structural alloy steel bars
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can GB/T 3077 20CrMnMo Be Substituted With IS 1570 (Part 7) 10Cr36Mo10H?
GB/T 3077 20CrMnMo and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
GB/T 3077 20CrMnMo
0 active listings and RFQs →
IS 1570 (Part 7) 10Cr36Mo10H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3077 20CrMnMo and IS 1570 (Part 7) 10Cr36Mo10H?
GB/T 3077 20CrMnMo specifies Cu which is not specified for IS 1570 (Part 7) 10Cr36Mo10H. IS 1570 (Part 7) 10Cr36Mo10H specifies Al (metallic) which is not specified for GB/T 3077 20CrMnMo.
Can GB/T 3077 20CrMnMo be substituted with IS 1570 (Part 7) 10Cr36Mo10H?
GB/T 3077 20CrMnMo and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.