GB/T 3077 20CrMnSi vs UNI 11234 100Cr6

Minimal Match — 45.4% match based on chemical composition and mechanical property overlap.

GB/T 3077 20CrMnSi (GB/T 3077:2015) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades. Both fall under the Alloy Steel category. GB/T 3077 20CrMnSi is typically used for hot-rolled or forged structural alloy steel bars, while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components. GB/T 3077 20CrMnSi is defined under Guobiao Standards (GB/T), originating from China, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.

As per chemical composition, GB/T 3077 20CrMnSi vs UNI 11234 100Cr6 is a 68.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 45.4%.

Frequently Compared With GB/T 3077 20CrMnSi:
IS 4367 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
68.1%
MECHANICAL MATCH
0%
OVERALL
45.4%
Specifications
Property GB/T 3077 20CrMnSi UNI 11234 100Cr6
Standard GB/T 3077:2015 UNI 11234:2007
Category Alloy Steel Alloy Steel
C (%) 0.17-0.23 0.93-1.05
Si (%) 0.90-1.20 0.15-0.35
Mn (%) 0.80-1.10 0.25-0.45
Cr (%) 0.80-1.10 1.35-1.65
P (%) <=0.030 <=0.025
S (%) <=0.030 <=0.025
Cu (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3077 20CrMnSi UNI 11234 100Cr6
Tensile Strength >=785 MPa 750-1000 MPa
Yield Strength >=635 MPa 400-600 MPa
Elongation >=12% 10-14 %
Hardness <=207 HB 60-64 HRC
Condition Quenched and tempered, test sample 25 mm; hardness is for bars delivered annealed or high temperature tempered Not specified
Typical Applications
GB/T 3077 20CrMnSi
Hot-rolled or forged structural alloy steel bars
UNI 11234 100Cr6
ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components
Key Differences
Can GB/T 3077 20CrMnSi Be Substituted With UNI 11234 100Cr6?
GB/T 3077 20CrMnSi and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GB/T 3077 20CrMnSi
No active listings currently.
UNI 11234 100Cr6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5700–6800 mm (224.41–267.72 in)
On M-EX Right Now
GB/T 3077 20CrMnSi
0 active listings and RFQs →
UNI 11234 100Cr6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3077 20CrMnSi and UNI 11234 100Cr6?
GB/T 3077 20CrMnSi specifies Cu which is not specified for UNI 11234 100Cr6.
Can GB/T 3077 20CrMnSi be substituted with UNI 11234 100Cr6?
GB/T 3077 20CrMnSi and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.