GB/T 3077 30Cr vs SAE J404 5130

Strong Match — 89.1% match based on chemical composition and mechanical property overlap.

GB/T 3077 30Cr (GB/T 3077:2015) and SAE J404 5130 (SAE J404:2000) are both steel grades. Both fall under the Alloy Steel category. GB/T 3077 30Cr is typically used for hot-rolled or forged structural alloy steel bars, while SAE J404 5130 is commonly used for chemistry-only alloy steel grade; see the composition notes for product scope. GB/T 3077 30Cr is defined under Guobiao Standards (GB/T), originating from China, while SAE J404 5130 is defined under SAE International, originating from United States.

As per chemical composition, GB/T 3077 30Cr vs SAE J404 5130 is a 89.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 89.1%.

Frequently Compared With GB/T 3077 30Cr:
IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6
Match Breakdown
CHEMISTRY MATCH
89.1%
MECHANICAL MATCH
No shared data
OVERALL
89.1%
Specifications
Property GB/T 3077 30Cr SAE J404 5130
Standard GB/T 3077:2015 SAE J404:2000
Category Alloy Steel Alloy Steel
C (%) 0.27-0.34 0.28-0.33
Si (%) 0.17-0.37 0.15-0.35
Mn (%) 0.50-0.80 0.70-0.90
Cr (%) 0.80-1.10 0.80-1.10
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.040
Cu (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3077 30Cr SAE J404 5130
Tensile Strength >=885 MPa Not specified
Yield Strength >=685 MPa Not specified
Elongation >=11% Not specified
Hardness <=187 HB Not specified
Condition Quenched and tempered, test sample 25 mm; hardness is for bars delivered annealed or high temperature tempered Not specified
Typical Applications
GB/T 3077 30Cr
Hot-rolled or forged structural alloy steel bars
SAE J404 5130
Chemistry-only alloy steel grade; see the composition notes for product scope
Key Differences
Can GB/T 3077 30Cr Be Substituted With SAE J404 5130?
GB/T 3077 30Cr and SAE J404 5130 overlap closely enough on chemistry and mechanical properties that SAE J404 5130 is often considered as a substitute for GB/T 3077 30Cr in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
GB/T 3077 30Cr
0 active listings and RFQs →
SAE J404 5130
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3077 30Cr and SAE J404 5130?
GB/T 3077 30Cr specifies Cu which is not specified for SAE J404 5130.
Can GB/T 3077 30Cr be substituted with SAE J404 5130?
GB/T 3077 30Cr and SAE J404 5130 overlap closely enough on chemistry and mechanical properties that SAE J404 5130 is often considered as a substitute for GB/T 3077 30Cr in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.