GB/T 3077 30Mn2 vs SAE J404 1330

Strong Match — 90.6% match based on chemical composition and mechanical property overlap.

GB/T 3077 30Mn2 (GB/T 3077:2015) and SAE J404 1330 (SAE J404:2000) are both steel grades. Both fall under the Alloy Steel category. GB/T 3077 30Mn2 is typically used for hot-rolled or forged structural alloy steel bars, while SAE J404 1330 is commonly used for chemistry-only alloy steel grade; see the composition notes for product scope. GB/T 3077 30Mn2 is defined under Guobiao Standards (GB/T), originating from China, while SAE J404 1330 is defined under SAE International, originating from United States.

As per chemical composition, GB/T 3077 30Mn2 vs SAE J404 1330 is a 90.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 90.6%.

Frequently Compared With GB/T 3077 30Mn2:
UNI 11234 100Cr6 IS 1570 (Part 7) 10Cr36Mo10H EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10
Match Breakdown
CHEMISTRY MATCH
90.6%
MECHANICAL MATCH
No shared data
OVERALL
90.6%
Specifications
Property GB/T 3077 30Mn2 SAE J404 1330
Standard GB/T 3077:2015 SAE J404:2000
Category Alloy Steel Alloy Steel
C (%) 0.27-0.34 0.28-0.33
Si (%) 0.17-0.37 0.15-0.35
Mn (%) 1.40-1.80 1.60-1.80
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.040
Cu (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3077 30Mn2 SAE J404 1330
Tensile Strength >=785 MPa Not specified
Yield Strength >=635 MPa Not specified
Elongation >=12% Not specified
Hardness <=207 HB Not specified
Condition Quenched and tempered, test sample 25 mm; hardness is for bars delivered annealed or high temperature tempered Not specified
Typical Applications
GB/T 3077 30Mn2
Hot-rolled or forged structural alloy steel bars
SAE J404 1330
Chemistry-only alloy steel grade; see the composition notes for product scope
Key Differences
Can GB/T 3077 30Mn2 Be Substituted With SAE J404 1330?
GB/T 3077 30Mn2 and SAE J404 1330 overlap closely enough on chemistry and mechanical properties that SAE J404 1330 is often considered as a substitute for GB/T 3077 30Mn2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
GB/T 3077 30Mn2
0 active listings and RFQs →
SAE J404 1330
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3077 30Mn2 and SAE J404 1330?
GB/T 3077 30Mn2 specifies Cu which is not specified for SAE J404 1330.
Can GB/T 3077 30Mn2 be substituted with SAE J404 1330?
GB/T 3077 30Mn2 and SAE J404 1330 overlap closely enough on chemistry and mechanical properties that SAE J404 1330 is often considered as a substitute for GB/T 3077 30Mn2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.