GB/T 3077 34CrNi2 vs GB/T 3077 20CrNi3

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

GB/T 3077 34CrNi2 (GB/T 3077:2015) and GB/T 3077 20CrNi3 (GB/T 3077:2015) are both steel grades. Both fall under the Alloy Steel category. GB/T 3077 34CrNi2 is typically used for hot-rolled or forged structural alloy steel bars, while GB/T 3077 20CrNi3 is commonly used for hot-rolled or forged structural alloy steel bars. GB/T 3077 34CrNi2 is defined under Guobiao Standards (GB/T), originating from China, while GB/T 3077 20CrNi3 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, GB/T 3077 34CrNi2 vs GB/T 3077 20CrNi3 is a 70.3% match. As per mechanical properties, the match is 100%. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With GB/T 3077 34CrNi2:
UNI 11234 100Cr6 IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
70.3%
MECHANICAL MATCH
100%
OVERALL
69.9%
Specifications
Property GB/T 3077 34CrNi2 GB/T 3077 20CrNi3
Standard GB/T 3077:2015 GB/T 3077:2015
Category Alloy Steel Alloy Steel
C (%) 0.30-0.37 0.17-0.24
Si (%) 0.17-0.37 0.17-0.37
Mn (%) 0.60-0.90 0.30-0.60
Cr (%) 0.80-1.10 0.60-0.90
Ni (%) 1.20-1.60 2.75-3.15
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.030
Cu (%) <=0.30 <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3077 34CrNi2 GB/T 3077 20CrNi3
Tensile Strength >=930 MPa >=930 MPa
Yield Strength >=735 MPa >=735 MPa
Elongation >=11% >=11%
Hardness <=241 HB <=241 HB
Condition Quenched and tempered, test sample 25 mm; hardness is for bars delivered annealed or high temperature tempered Quenched and tempered, test sample 25 mm; hardness is for bars delivered annealed or high temperature tempered
Typical Applications
GB/T 3077 34CrNi2
Hot-rolled or forged structural alloy steel bars
GB/T 3077 20CrNi3
Hot-rolled or forged structural alloy steel bars
Can GB/T 3077 34CrNi2 Be Substituted With GB/T 3077 20CrNi3?
GB/T 3077 34CrNi2 and GB/T 3077 20CrNi3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
GB/T 3077 34CrNi2
0 active listings and RFQs →
GB/T 3077 20CrNi3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3077 34CrNi2 and GB/T 3077 20CrNi3?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can GB/T 3077 34CrNi2 be substituted with GB/T 3077 20CrNi3?
GB/T 3077 34CrNi2 and GB/T 3077 20CrNi3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.