Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
Cr
Mo
V
P
S
Cu
0.30-0.38
0.17-0.37
0.40-0.70
1.00-1.30
0.20-0.30
0.10-0.20
<=0.030
<=0.030
<=0.30
Mechanical Properties
Tensile Strength
>=1080 MPa
Yield Strength
>=930 MPa
Elongation
>=10%
Hardness
<=241 HB
Condition
Quenched and tempered, test sample 25 mm; hardness is for bars delivered annealed or high temperature tempered
More data from GB/T 3077:2015
From the standard
Recommended heat treatment5 settings
Test sample size
25 mm
Quenching temperature
900 deg C
Quenching coolant
oil
Tempering temperature
630 deg C
Tempering coolant
water, oil
Allowable deviation: quenching +/-15 deg C, low temperature tempering +/-20 deg C, high temperature tempering +/-50 deg C.
Source: GB/T 3077:2015, Table 3
Mechanical properties, quenched and tempered6 values
Test sample size
25 mm
Tensile strength Rm, min
1080 MPa
Lower yield strength ReL, min
930 MPa
Elongation after fracture A, min
10 %
Reduction of area Z, min
50 %
Impact absorbed energy KU2, min
71 J
Minimum values after the recommended heat treatment; if sample is larger than the bar, treat the actual bar.
Source: GB/T 3077:2015, Table 3
Brinell hardness, annealed or high temperature tempered1 value
Brinell hardness HBW, max
241
For steel bars delivered annealed or high temperature tempered.
Source: GB/T 3077:2015, Table 3