GB/T 3077 40CrMnMo vs SAE J404 4140

Close Alternative — 78.2% match based on chemical composition and mechanical property overlap.

GB/T 3077 40CrMnMo (GB/T 3077:2015) and SAE J404 4140 (SAE J404:2000) are both steel grades. Both fall under the Alloy Steel category. GB/T 3077 40CrMnMo is typically used for hot-rolled or forged structural alloy steel bars, while SAE J404 4140 is commonly used for chemistry-only alloy steel grade; see the composition notes for product scope. GB/T 3077 40CrMnMo is defined under Guobiao Standards (GB/T), originating from China, while SAE J404 4140 is defined under SAE International, originating from United States.

As per chemical composition, GB/T 3077 40CrMnMo vs SAE J404 4140 is a 78.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 78.2%.

Frequently Compared With GB/T 3077 40CrMnMo:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6
Match Breakdown
CHEMISTRY MATCH
78.2%
MECHANICAL MATCH
No shared data
OVERALL
78.2%
Specifications
Property GB/T 3077 40CrMnMo SAE J404 4140
Standard GB/T 3077:2015 SAE J404:2000
Category Alloy Steel Alloy Steel
C (%) 0.37-0.45 0.38-0.43
Si (%) 0.17-0.37 0.15-0.35
Mn (%) 0.90-1.20 0.75-1.00
Cr (%) 0.90-1.20 0.80-1.10
Mo (%) 0.20-0.30 0.15-0.25
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.040
Cu (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 3077 40CrMnMo SAE J404 4140
Tensile Strength >=980 MPa Not specified
Yield Strength >=785 MPa Not specified
Elongation >=10% Not specified
Hardness <=217 HB Not specified
Condition Quenched and tempered, test sample 25 mm; hardness is for bars delivered annealed or high temperature tempered Not specified
Typical Applications
GB/T 3077 40CrMnMo
Hot-rolled or forged structural alloy steel bars
SAE J404 4140
Chemistry-only alloy steel grade; see the composition notes for product scope
Key Differences
Can GB/T 3077 40CrMnMo Be Substituted With SAE J404 4140?
GB/T 3077 40CrMnMo and SAE J404 4140 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
GB/T 3077 40CrMnMo
0 active listings and RFQs →
SAE J404 4140
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 3077 40CrMnMo and SAE J404 4140?
GB/T 3077 40CrMnMo specifies Cu which is not specified for SAE J404 4140.
Can GB/T 3077 40CrMnMo be substituted with SAE J404 4140?
GB/T 3077 40CrMnMo and SAE J404 4140 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.