GB/T 699 85 vs BS 970 (Part 1) 045M10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

GB/T 699 85 (GB/T 699:2015) and BS 970 (Part 1) 045M10 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Carbon Steel category. GB/T 699 85 is typically used for hot-rolled or forged quality carbon structural steel bars up to 250 mm, while BS 970 (Part 1) 045M10 is commonly used for case hardening steel (section four). GB/T 699 85 is defined under Guobiao Standards (GB/T), originating from China, while BS 970 (Part 1) 045M10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, GB/T 699 85 vs BS 970 (Part 1) 045M10 is a 63.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With GB/T 699 85:
BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 060A40 BS 970 (Part 1) 060A45
Match Breakdown
CHEMISTRY MATCH
63.1%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property GB/T 699 85 BS 970 (Part 1) 045M10
Standard GB/T 699:2015 BS 970 (Part 1):1991
Category Carbon Steel Carbon Steel
C (%) 0.82-0.90 0.07-0.13
Si (%) 0.17-0.37 Not specified
Mn (%) 0.50-0.80 0.30-0.60
P (%) <=0.035 Not specified
S (%) <=0.035 Not specified
Cr (%) <=0.25 Not specified
Ni (%) <=0.30 Not specified
Cu (%) <=0.25 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 699 85 BS 970 (Part 1) 045M10
Tensile Strength >=1130 MPa 430 MPa min
Yield Strength >=980 MPa Not specified
Elongation >=6% 18 % min
Hardness <=302 HB (as delivered, not heat treated) Not specified
Condition Quenched and tempered sample (with working allowance), bars up to 80 mm; hardness for delivery state Case hardened, 19 mm test bar
Typical Applications
GB/T 699 85
Hot-rolled or forged quality carbon structural steel bars up to 250 mm
BS 970 (Part 1) 045M10
Case hardening steel (section four)
Key Differences
Can GB/T 699 85 Be Substituted With BS 970 (Part 1) 045M10?
GB/T 699 85 and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
GB/T 699 85
0 active listings and RFQs →
BS 970 (Part 1) 045M10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 699 85 and BS 970 (Part 1) 045M10?
GB/T 699 85 specifies Si, P, S, Cr which are not specified for BS 970 (Part 1) 045M10.
Can GB/T 699 85 be substituted with BS 970 (Part 1) 045M10?
GB/T 699 85 and BS 970 (Part 1) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.