Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
GB/T 699 35 (GB/T 699:2015) and BS 970 (Part 1) 040A04 (BS 970 (Part 1):1991) are both steel grades.
Both fall under the Carbon Steel category.
GB/T 699 35 is typically used for used for shafts, connecting rods, bolts, forged parts, gears, and machine components., while BS 970 (Part 1) 040A04 is commonly used for as-rolled, or as-rolled and softened, steel (section two).
GB/T 699 35 is defined under Guobiao Standards (GB/T), originating from China, while BS 970 (Part 1) 040A04 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, GB/T 699 35 vs BS 970 (Part 1) 040A04 is a 62% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
GB/T 699 35
BS 970 (Part 1) 040A04
Tensile Strength
>=530 MPa
Not specified
Yield Strength
>=315 MPa
Not specified
Elongation
>=20%
Not specified
Hardness
<=197 HB (as delivered, not heat treated)
Not specified
Condition
Normalized 25 mm sample blank, bars up to 80 mm; hardness for delivery state
Not specified
Typical Applications
GB/T 699 35
Used for shafts, connecting rods, bolts, forged parts, gears, and machine components.
BS 970 (Part 1) 040A04
As-rolled, or as-rolled and softened, steel (section two)
Key Differences
GB/T 699 35 specifies Si, P, S, Cr which are not specified for BS 970 (Part 1) 040A04.
Can GB/T 699 35 Be Substituted With BS 970 (Part 1) 040A04?
GB/T 699 35 and BS 970 (Part 1) 040A04 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between GB/T 699 35 and BS 970 (Part 1) 040A04?
GB/T 699 35 specifies Si, P, S, Cr which are not specified for BS 970 (Part 1) 040A04.
Can GB/T 699 35 be substituted with BS 970 (Part 1) 040A04?
GB/T 699 35 and BS 970 (Part 1) 040A04 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.