GB/T 700 Q235C vs AS/NZS 3679.1 350

Related Material — 64.4% match based on chemical composition and mechanical property overlap.

GB/T 700 Q235C (GB/T 700:2006) and AS/NZS 3679.1 350 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. GB/T 700 Q235C is typically used for hot rolled structural sheets, strips, sections and bars for welding, riveting and bolting engineering, while AS/NZS 3679.1 350 is commonly used for hot-rolled structural bars and sections for primary structural beams, columns, and framing. GB/T 700 Q235C is defined under Guobiao Standards (GB/T), originating from China, while AS/NZS 3679.1 350 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, GB/T 700 Q235C vs AS/NZS 3679.1 350 is a 95.3% match. As per mechanical properties, the match is 2.5%. Combined, this makes them a related material overall at 64.4%.

Frequently Compared With GB/T 700 Q235C:
ASTM A283C CSA G40.21 260W CSA G40.21 350W ASTM A1008 SS Grade 80 GOST 19281 09G2S AS/NZS 3679.1 300 CSA G40.21 300W CSA G40.21 400A CSA G40.21 400W CSA G40.21 480W ASTM A1008 SS Grade 50 ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
95.3%
MECHANICAL MATCH
2.5%
OVERALL
64.4%
Specifications
Property GB/T 700 Q235C AS/NZS 3679.1 350
Standard GB/T 700:2006 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
C (%) <=0.17 <=0.22
Si (%) <=0.35 <=0.50
Mn (%) <=1.40 <=1.70
P (%) <=0.040 <=0.040
S (%) <=0.040 <=0.040
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GB/T 700 Q235C AS/NZS 3679.1 350
Tensile Strength 370-500 MPa 480-640 MPa
Yield Strength >=235 MPa 350 MPa min
Elongation >=26% 20% min
Condition Hot rolled, controlled rolled or normalized; yield up to 16 mm, elongation up to 40 mm (N/mm2 = MPa) Not specified
Typical Applications
GB/T 700 Q235C
Hot rolled structural sheets, strips, sections and bars for welding, riveting and bolting engineering
AS/NZS 3679.1 350
Hot-rolled structural bars and sections for primary structural beams, columns, and framing
Can GB/T 700 Q235C Be Substituted With AS/NZS 3679.1 350?
GB/T 700 Q235C and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
GB/T 700 Q235C
No active listings currently.
AS/NZS 3679.1 350
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3200 mm (114.17–125.98 in)
On M-EX Right Now
GB/T 700 Q235C
0 active listings and RFQs →
AS/NZS 3679.1 350
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between GB/T 700 Q235C and AS/NZS 3679.1 350?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can GB/T 700 Q235C be substituted with AS/NZS 3679.1 350?
GB/T 700 Q235C and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.