Strong Match — 87.7% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 13Ni13Cr3 (IS 11169 (Part 1):1984) and IS 4367 13Ni13Cr3 (IS 4367:1991) are both steel grades.
Both fall under the Alloy Steel category.
IS 11169 (Part 1) 13Ni13Cr3 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while IS 4367 13Ni13Cr3 is commonly used for gears, pinion gears, camshafts, transmission parts, aircraft components, heavy duty shafts.
IS 11169 (Part 1) 13Ni13Cr3 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 13Ni13Cr3 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 11169 (Part 1) 13Ni13Cr3 vs IS 4367 13Ni13Cr3 is a 98.3% match.
As per mechanical properties, the match is 66.7%.
Combined, this makes them a strong match overall at 87.7%.
Frequently Compared With IS 11169 (Part 1) 13Ni13Cr3:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 13Ni13Cr3
IS 4367 13Ni13Cr3
Core Tensile Strength
>=850 MPa (60 mm) / >=800 MPa (100 mm)
Not specified
Core Elongation
>=12% (60 mm)
Not specified
Hardness, annealed
<=190 HB
Not specified
Tensile Strength
Not specified
850 MPa min
Elongation
Not specified
>=12%
Izod Impact
Not specified
48 J min
Hardness (soft annealed)
Not specified
<=229 HB
Condition
Not specified
Refined, quenched and stress relieved (core properties), ruling section up to 60 mm
Typical Applications
IS 11169 (Part 1) 13Ni13Cr3
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 4367 13Ni13Cr3 specifies S, P which are not specified for IS 11169 (Part 1) 13Ni13Cr3.
Can IS 11169 (Part 1) 13Ni13Cr3 Be Substituted With IS 4367 13Ni13Cr3?
IS 11169 (Part 1) 13Ni13Cr3 and IS 4367 13Ni13Cr3 overlap closely enough on chemistry and mechanical properties that IS 4367 13Ni13Cr3 is often considered as a substitute for IS 11169 (Part 1) 13Ni13Cr3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 11169 (Part 1) 13Ni13Cr3 and IS 4367 13Ni13Cr3?
IS 4367 13Ni13Cr3 specifies S, P which are not specified for IS 11169 (Part 1) 13Ni13Cr3.
Can IS 11169 (Part 1) 13Ni13Cr3 be substituted with IS 4367 13Ni13Cr3?
IS 11169 (Part 1) 13Ni13Cr3 and IS 4367 13Ni13Cr3 overlap closely enough on chemistry and mechanical properties that IS 4367 13Ni13Cr3 is often considered as a substitute for IS 11169 (Part 1) 13Ni13Cr3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.