IS 11169 (Part 1) 14C6 vs BS 970 (Part 1) 080M15

Strong Match — 93.1% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 14C6 (IS 11169 (Part 1):1984) and BS 970 (Part 1) 080M15 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Carbon Steel category. IS 11169 (Part 1) 14C6 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while BS 970 (Part 1) 080M15 is commonly used for wrought steel supplied as bright bar for mechanical and allied engineering purposes (table 4).. IS 11169 (Part 1) 14C6 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 080M15 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 1) 14C6 vs BS 970 (Part 1) 080M15 is a 93.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 93.1%.

Frequently Compared With IS 11169 (Part 1) 14C6:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A12 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A32 BS 970 (Part 3) 045A10
Match Breakdown
CHEMISTRY MATCH
93.1%
MECHANICAL MATCH
No shared data
OVERALL
93.1%
Specifications
Property IS 11169 (Part 1) 14C6 BS 970 (Part 1) 080M15
Standard IS 11169 (Part 1):1984 BS 970 (Part 1):1983
Category Carbon Steel Carbon Steel
C (%) 0.10-0.18 0.12-0.18
Mn (%) 0.40-0.70 0.60-1.00
P (%) Not specified <=0.050
S (%) Not specified <=0.050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 14C6 BS 970 (Part 1) 080M15
Core Tensile Strength >=500 MPa (Over 15 up to 30 mm) Not specified
Core Elongation >=17% (Over 15 up to 30 mm) Not specified
Hardness, annealed <=140 HB Not specified
Typical Applications
IS 11169 (Part 1) 14C6
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
BS 970 (Part 1) 080M15
Wrought steel supplied as bright bar for mechanical and allied engineering purposes (Table 4).
Key Differences
Can IS 11169 (Part 1) 14C6 Be Substituted With BS 970 (Part 1) 080M15?
IS 11169 (Part 1) 14C6 and BS 970 (Part 1) 080M15 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 080M15 is often considered as a substitute for IS 11169 (Part 1) 14C6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 1) 14C6
0 active listings and RFQs →
BS 970 (Part 1) 080M15
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 14C6 and BS 970 (Part 1) 080M15?
BS 970 (Part 1) 080M15 specifies P, S which are not specified for IS 11169 (Part 1) 14C6.
Can IS 11169 (Part 1) 14C6 be substituted with BS 970 (Part 1) 080M15?
IS 11169 (Part 1) 14C6 and BS 970 (Part 1) 080M15 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 080M15 is often considered as a substitute for IS 11169 (Part 1) 14C6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.