Strong Match — 95.8% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 15C8 (IS 11169 (Part 1):1984) and IS 11169 (Part 1) 14C6 (IS 11169 (Part 1):1984) are both steel grades.
Both fall under the Carbon Steel category.
IS 11169 (Part 1) 15C8 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while IS 11169 (Part 1) 14C6 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1).
IS 11169 (Part 1) 15C8 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 14C6 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 11169 (Part 1) 15C8 vs IS 11169 (Part 1) 14C6 is a 93.7% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 95.8%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 15C8
IS 11169 (Part 1) 14C6
Hardness, annealed
<=140 HB
<=140 HB
Core Tensile Strength
Not specified
>=500 MPa (Over 15 up to 30 mm)
Core Elongation
Not specified
>=17% (Over 15 up to 30 mm)
Typical Applications
IS 11169 (Part 1) 15C8
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 11169 (Part 1) 14C6
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Can IS 11169 (Part 1) 15C8 Be Substituted With IS 11169 (Part 1) 14C6?
IS 11169 (Part 1) 15C8 and IS 11169 (Part 1) 14C6 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 14C6 is often considered as a substitute for IS 11169 (Part 1) 15C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 11169 (Part 1) 15C8 and IS 11169 (Part 1) 14C6?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 1) 15C8 be substituted with IS 11169 (Part 1) 14C6?
IS 11169 (Part 1) 15C8 and IS 11169 (Part 1) 14C6 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 14C6 is often considered as a substitute for IS 11169 (Part 1) 15C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.