Post Stock Login Register

IS 11169 (Part 1) 15Ni16Cr5 vs IS 11169 (Part 1) 10Ni5Cr4

Minimal Match — 43.7% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 15Ni16Cr5 (IS 11169 (Part 1):1984) and IS 11169 (Part 1) 10Ni5Cr4 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 15Ni16Cr5 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while IS 11169 (Part 1) 10Ni5Cr4 is commonly used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b). IS 11169 (Part 1) 15Ni16Cr5 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 10Ni5Cr4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 11169 (Part 1) 15Ni16Cr5 vs IS 11169 (Part 1) 10Ni5Cr4 is a 65.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 43.7%.

Frequently Compared With IS 11169 (Part 1) 15Ni16Cr5:
IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 4367 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
65.6%
MECHANICAL MATCH
0%
OVERALL
43.7%
Specifications
Property IS 11169 (Part 1) 15Ni16Cr5 IS 11169 (Part 1) 10Ni5Cr4
Standard IS 11169 (Part 1):1984 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.07-0.12
Si (%) 0.10-0.35 <=0.30
Mn (%) 0.40-0.70 0.60-0.90
Ni (%) 3.80-4.30 1.20-1.50
Cr (%) 1.00-1.40 0.90-1.20
Cu (%) Not specified <=0.25
P (%) Not specified <=0.025
S (%) Not specified <=0.025
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 15Ni16Cr5 IS 11169 (Part 1) 10Ni5Cr4
Core Tensile Strength >=1350 MPa (30 mm) / >=1200 MPa (60 mm) / >=1150 MPa (90 mm) Not specified
Core Elongation >=9% (30 mm) Not specified
Hardness, annealed <=200 HB Not specified
Hardness, ferrite-pearlite (+FP) Not specified 137-187 HB
Tensile Strength, annealed (+AC) Not specified <=520 MPa (over 5 to 40 mm)
Typical Applications
IS 11169 (Part 1) 15Ni16Cr5
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 11169 (Part 1) 10Ni5Cr4
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
Can IS 11169 (Part 1) 15Ni16Cr5 Be Substituted With IS 11169 (Part 1) 10Ni5Cr4?
IS 11169 (Part 1) 15Ni16Cr5 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 1) 15Ni16Cr5
0 active listings and RFQs →
IS 11169 (Part 1) 10Ni5Cr4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 15Ni16Cr5 and IS 11169 (Part 1) 10Ni5Cr4?
IS 11169 (Part 1) 10Ni5Cr4 specifies Cu, P, S which are not specified for IS 11169 (Part 1) 15Ni16Cr5.
Can IS 11169 (Part 1) 15Ni16Cr5 be substituted with IS 11169 (Part 1) 10Ni5Cr4?
IS 11169 (Part 1) 15Ni16Cr5 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.