IS 11169 (Part 1) 15Ni5Cr4Mo1 vs IS 11169 (Part 1) 15Ni5Cr4Mo1
Strong Match — 97.6% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 15Ni5Cr4Mo1 (IS 11169 (Part 1):1984) and IS 11169 (Part 1) 15Ni5Cr4Mo1 (IS 11169 (Part 1):2022) are both steel grades.
Both fall under the Alloy Steel category.
IS 11169 (Part 1) 15Ni5Cr4Mo1 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while IS 11169 (Part 1) 15Ni5Cr4Mo1 is commonly used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b).
IS 11169 (Part 1) 15Ni5Cr4Mo1 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 15Ni5Cr4Mo1 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 11169 (Part 1) 15Ni5Cr4Mo1 vs IS 11169 (Part 1) 15Ni5Cr4Mo1 is a 96.4% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 97.6%.
Frequently Compared With IS 11169 (Part 1) 15Ni5Cr4Mo1:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 15Ni5Cr4Mo1
IS 11169 (Part 1) 15Ni5Cr4Mo1
Core Tensile Strength
>=1000 MPa (30 mm) / >=950 MPa (90 mm)
Not specified
Core Elongation
>=9% (30 mm)
Not specified
Hardness, annealed
<=180 HB
Not specified
Hardness, annealed (+AC)
Not specified
<=180 HBW
Typical Applications
IS 11169 (Part 1) 15Ni5Cr4Mo1
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 11169 (Part 1) 15Ni5Cr4Mo1
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
IS 11169 (Part 1) 15Ni5Cr4Mo1 specifies Cu, P, S which are not specified for IS 11169 (Part 1) 15Ni5Cr4Mo1.
Can IS 11169 (Part 1) 15Ni5Cr4Mo1 Be Substituted With IS 11169 (Part 1) 15Ni5Cr4Mo1?
IS 11169 (Part 1) 15Ni5Cr4Mo1 and IS 11169 (Part 1) 15Ni5Cr4Mo1 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 15Ni5Cr4Mo1 is often considered as a substitute for IS 11169 (Part 1) 15Ni5Cr4Mo1 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 11169 (Part 1) 15Ni5Cr4Mo1 and IS 11169 (Part 1) 15Ni5Cr4Mo1?
IS 11169 (Part 1) 15Ni5Cr4Mo1 specifies Cu, P, S which are not specified for IS 11169 (Part 1) 15Ni5Cr4Mo1.
Can IS 11169 (Part 1) 15Ni5Cr4Mo1 be substituted with IS 11169 (Part 1) 15Ni5Cr4Mo1?
IS 11169 (Part 1) 15Ni5Cr4Mo1 and IS 11169 (Part 1) 15Ni5Cr4Mo1 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 15Ni5Cr4Mo1 is often considered as a substitute for IS 11169 (Part 1) 15Ni5Cr4Mo1 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.