IS 11169 (Part 1) 15Ni5Cr4Mo1 vs IS 4367 15Ni5Cr4Mo1

Strong Match — 87.7% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 15Ni5Cr4Mo1 (IS 11169 (Part 1):1984) and IS 4367 15Ni5Cr4Mo1 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 15Ni5Cr4Mo1 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 15Ni5Cr4Mo1 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 11169 (Part 1) 15Ni5Cr4Mo1 vs IS 4367 15Ni5Cr4Mo1 is a 98.3% match. As per mechanical properties, the match is 66.7%. Combined, this makes them a strong match overall at 87.7%.

Frequently Compared With IS 11169 (Part 1) 15Ni5Cr4Mo1:
IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 10Cr36Mo10H NF A35-565 100C6 IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6
Match Breakdown
CHEMISTRY MATCH
98.3%
MECHANICAL MATCH
66.7%
OVERALL
87.7%
Specifications
Property IS 11169 (Part 1) 15Ni5Cr4Mo1 IS 4367 15Ni5Cr4Mo1
Standard IS 11169 (Part 1):1984 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.12-0.18
Si (%) 0.10-0.35 0.10-0.35
Mn (%) 0.60-1.00 0.60-1.00
Ni (%) 1.00-1.50 1.00-1.50
Cr (%) 0.75-1.25 0.75-1.25
Mo (%) 0.08-0.15 0.08-0.15
S (%) Not specified <=0.035
P (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 15Ni5Cr4Mo1 IS 4367 15Ni5Cr4Mo1
Core Tensile Strength >=1000 MPa (30 mm) / >=950 MPa (90 mm) Not specified
Core Elongation >=9% (30 mm) Not specified
Hardness, annealed <=180 HB Not specified
Tensile Strength Not specified 1000 MPa min
Elongation Not specified >=9%
Izod Impact Not specified 41 J min
Hardness (soft annealed) Not specified <=217 HB
Condition Not specified Refined, quenched and stress relieved (core properties), ruling section up to 30 mm
Typical Applications
IS 11169 (Part 1) 15Ni5Cr4Mo1
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 4367 15Ni5Cr4Mo1
Not documented
Key Differences
Can IS 11169 (Part 1) 15Ni5Cr4Mo1 Be Substituted With IS 4367 15Ni5Cr4Mo1?
IS 11169 (Part 1) 15Ni5Cr4Mo1 and IS 4367 15Ni5Cr4Mo1 overlap closely enough on chemistry and mechanical properties that IS 4367 15Ni5Cr4Mo1 is often considered as a substitute for IS 11169 (Part 1) 15Ni5Cr4Mo1 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 1) 15Ni5Cr4Mo1
0 active listings and RFQs →
IS 4367 15Ni5Cr4Mo1
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 15Ni5Cr4Mo1 and IS 4367 15Ni5Cr4Mo1?
IS 4367 15Ni5Cr4Mo1 specifies S, P which are not specified for IS 11169 (Part 1) 15Ni5Cr4Mo1.
Can IS 11169 (Part 1) 15Ni5Cr4Mo1 be substituted with IS 4367 15Ni5Cr4Mo1?
IS 11169 (Part 1) 15Ni5Cr4Mo1 and IS 4367 15Ni5Cr4Mo1 overlap closely enough on chemistry and mechanical properties that IS 4367 15Ni5Cr4Mo1 is often considered as a substitute for IS 11169 (Part 1) 15Ni5Cr4Mo1 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.