IS 11169 (Part 1) 16Ni3Cr2 vs BS 970 (Part 3) 637M17

Close Alternative — 82.6% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 16Ni3Cr2 (IS 11169 (Part 1):1984) and BS 970 (Part 3) 637M17 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 16Ni3Cr2 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while BS 970 (Part 3) 637M17 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy case hardening steel (table 15). IS 11169 (Part 1) 16Ni3Cr2 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 3) 637M17 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 1) 16Ni3Cr2 vs BS 970 (Part 3) 637M17 is a 82.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 82.6%.

Frequently Compared With IS 11169 (Part 1) 16Ni3Cr2:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 UNI 11234 100Cr6 IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
82.6%
MECHANICAL MATCH
No shared data
OVERALL
82.6%
Specifications
Property IS 11169 (Part 1) 16Ni3Cr2 BS 970 (Part 3) 637M17
Standard IS 11169 (Part 1):1984 BS 970 (Part 3):1991
Category Alloy Steel Alloy Steel
C (%) 0.12-0.20 0.14-0.20
Si (%) 0.10-0.35 0.10-0.40
Mn (%) 0.60-1.00 0.60-0.90
Ni (%) 0.60-1.00 0.85-1.25
Cr (%) 0.40-0.80 0.60-1.00
P (%) Not specified <=0.04
S (%) Not specified <=0.05
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 16Ni3Cr2 BS 970 (Part 3) 637M17
Core Tensile Strength >=700 MPa (30 mm) Not specified
Core Elongation >=15% (30 mm) Not specified
Hardness, annealed <=160 HB Not specified
Typical Applications
IS 11169 (Part 1) 16Ni3Cr2
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
BS 970 (Part 3) 637M17
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy case hardening steel (Table 15)
Key Differences
Can IS 11169 (Part 1) 16Ni3Cr2 Be Substituted With BS 970 (Part 3) 637M17?
IS 11169 (Part 1) 16Ni3Cr2 and BS 970 (Part 3) 637M17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 11169 (Part 1) 16Ni3Cr2
0 active listings and RFQs →
BS 970 (Part 3) 637M17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 16Ni3Cr2 and BS 970 (Part 3) 637M17?
BS 970 (Part 3) 637M17 specifies P, S which are not specified for IS 11169 (Part 1) 16Ni3Cr2.
Can IS 11169 (Part 1) 16Ni3Cr2 be substituted with BS 970 (Part 3) 637M17?
IS 11169 (Part 1) 16Ni3Cr2 and BS 970 (Part 3) 637M17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.