IS 11169 (Part 1) 16Ni3Cr2 vs IS 11169 (Part 1) 10Ni5Cr4
Minimal Match — 43.5% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 16Ni3Cr2 (IS 11169 (Part 1):1984) and IS 11169 (Part 1) 10Ni5Cr4 (IS 11169 (Part 1):2022) are both steel grades.
Both fall under the Alloy Steel category.
IS 11169 (Part 1) 16Ni3Cr2 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while IS 11169 (Part 1) 10Ni5Cr4 is commonly used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b).
IS 11169 (Part 1) 16Ni3Cr2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 10Ni5Cr4 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 11169 (Part 1) 16Ni3Cr2 vs IS 11169 (Part 1) 10Ni5Cr4 is a 65.3% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 43.5%.
Frequently Compared With IS 11169 (Part 1) 16Ni3Cr2:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 16Ni3Cr2
IS 11169 (Part 1) 10Ni5Cr4
Core Tensile Strength
>=700 MPa (30 mm)
Not specified
Core Elongation
>=15% (30 mm)
Not specified
Hardness, annealed
<=160 HB
Not specified
Hardness, ferrite-pearlite (+FP)
Not specified
137-187 HB
Tensile Strength, annealed (+AC)
Not specified
<=520 MPa (over 5 to 40 mm)
Typical Applications
IS 11169 (Part 1) 16Ni3Cr2
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 11169 (Part 1) 10Ni5Cr4
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
IS 11169 (Part 1) 10Ni5Cr4 specifies Cu, P, S which are not specified for IS 11169 (Part 1) 16Ni3Cr2.
Can IS 11169 (Part 1) 16Ni3Cr2 Be Substituted With IS 11169 (Part 1) 10Ni5Cr4?
IS 11169 (Part 1) 16Ni3Cr2 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 1) 16Ni3Cr2 and IS 11169 (Part 1) 10Ni5Cr4?
IS 11169 (Part 1) 10Ni5Cr4 specifies Cu, P, S which are not specified for IS 11169 (Part 1) 16Ni3Cr2.
Can IS 11169 (Part 1) 16Ni3Cr2 be substituted with IS 11169 (Part 1) 10Ni5Cr4?
IS 11169 (Part 1) 16Ni3Cr2 and IS 11169 (Part 1) 10Ni5Cr4 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.