Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 20Ni7Mo2 (IS 11169 (Part 1):1984) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades.
Both fall under the Alloy Steel category.
IS 11169 (Part 1) 20Ni7Mo2 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components.
IS 11169 (Part 1) 20Ni7Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.
As per chemical composition, IS 11169 (Part 1) 20Ni7Mo2 vs UNI 11234 100Cr6 is a 56% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 11169 (Part 1) 20Ni7Mo2:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 20Ni7Mo2
UNI 11234 100Cr6
Core Tensile Strength
>=850 MPa (30 mm) / >=700 MPa (60 mm)
Not specified
Core Elongation
>=12% (30 mm)
Not specified
Hardness, annealed
<=180 HB
Not specified
Tensile Strength
Not specified
750-1000 MPa
Yield Strength
Not specified
400-600 MPa
Elongation
Not specified
10-14 %
Hardness
Not specified
60-64 HRC
Typical Applications
IS 11169 (Part 1) 20Ni7Mo2
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 11169 (Part 1) 20Ni7Mo2 specifies Ni, Mo which are not specified for UNI 11234 100Cr6.
UNI 11234 100Cr6 specifies P, S, Cr which are not specified for IS 11169 (Part 1) 20Ni7Mo2.
Can IS 11169 (Part 1) 20Ni7Mo2 Be Substituted With UNI 11234 100Cr6?
IS 11169 (Part 1) 20Ni7Mo2 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 1) 20Ni7Mo2 and UNI 11234 100Cr6?
IS 11169 (Part 1) 20Ni7Mo2 specifies Ni, Mo which are not specified for UNI 11234 100Cr6. UNI 11234 100Cr6 specifies P, S, Cr which are not specified for IS 11169 (Part 1) 20Ni7Mo2.
Can IS 11169 (Part 1) 20Ni7Mo2 be substituted with UNI 11234 100Cr6?
IS 11169 (Part 1) 20Ni7Mo2 and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.