IS 11169 (Part 1) 30C8 vs IS 11169 (Part 1) 35C8

Strong Match — 96.2% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 30C8 (IS 11169 (Part 1):1984) and IS 11169 (Part 1) 35C8 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Carbon Steel category. IS 11169 (Part 1) 30C8 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while IS 11169 (Part 1) 35C8 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1). IS 11169 (Part 1) 30C8 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 35C8 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 11169 (Part 1) 30C8 vs IS 11169 (Part 1) 35C8 is a 94.3% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 96.2%.

Frequently Compared With IS 11169 (Part 1) 30C8:
BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
94.3%
MECHANICAL MATCH
100%
OVERALL
96.2%
Specifications
Property IS 11169 (Part 1) 30C8 IS 11169 (Part 1) 35C8
Standard IS 11169 (Part 1):1984 IS 11169 (Part 1):1984
Category Carbon Steel Carbon Steel
C (%) 0.25-0.35 0.30-0.40
Mn (%) 0.60-0.90 0.60-0.90
Si (%) 0.10-0.35 0.10-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 30C8 IS 11169 (Part 1) 35C8
Hardness, annealed <=160 HB <=160 HB
Tensile Strength (hardened and tempered) Not specified 620-770 MPa (16 mm) / 580-730 MPa (40 mm) / 540-690 MPa (100 mm)
0.2% Proof Stress Not specified >=420 MPa (16 mm) / >=365 MPa (40 mm) / >=325 MPa (100 mm)
Elongation Not specified >=17% (16 mm) / >=19% (40 mm) / >=20% (100 mm)
Typical Applications
IS 11169 (Part 1) 30C8
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 11169 (Part 1) 35C8
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Can IS 11169 (Part 1) 30C8 Be Substituted With IS 11169 (Part 1) 35C8?
IS 11169 (Part 1) 30C8 and IS 11169 (Part 1) 35C8 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 35C8 is often considered as a substitute for IS 11169 (Part 1) 30C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 1) 30C8
0 active listings and RFQs →
IS 11169 (Part 1) 35C8
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 30C8 and IS 11169 (Part 1) 35C8?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 1) 30C8 be substituted with IS 11169 (Part 1) 35C8?
IS 11169 (Part 1) 30C8 and IS 11169 (Part 1) 35C8 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 35C8 is often considered as a substitute for IS 11169 (Part 1) 30C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.