Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 34C14BT (IS 11169 (Part 1):1984) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades.
Both fall under the Alloy Steel category.
IS 11169 (Part 1) 34C14BT is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components.
IS 11169 (Part 1) 34C14BT is defined under Bureau of Indian Standards (IS), originating from India, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.
As per chemical composition, IS 11169 (Part 1) 34C14BT vs UNI 11234 100Cr6 is a 67.4% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 11169 (Part 1) 34C14BT:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 34C14BT
UNI 11234 100Cr6
Hardness, annealed
<=190 HB
Not specified
Tensile Strength
Not specified
750-1000 MPa
Yield Strength
Not specified
400-600 MPa
Elongation
Not specified
10-14 %
Hardness
Not specified
60-64 HRC
Typical Applications
IS 11169 (Part 1) 34C14BT
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 11169 (Part 1) 34C14BT specifies B which is not specified for UNI 11234 100Cr6.
UNI 11234 100Cr6 specifies P, S, Cr which are not specified for IS 11169 (Part 1) 34C14BT.
Can IS 11169 (Part 1) 34C14BT Be Substituted With UNI 11234 100Cr6?
IS 11169 (Part 1) 34C14BT and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 1) 34C14BT and UNI 11234 100Cr6?
IS 11169 (Part 1) 34C14BT specifies B which is not specified for UNI 11234 100Cr6. UNI 11234 100Cr6 specifies P, S, Cr which are not specified for IS 11169 (Part 1) 34C14BT.
Can IS 11169 (Part 1) 34C14BT be substituted with UNI 11234 100Cr6?
IS 11169 (Part 1) 34C14BT and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.