IS 11169 (Part 1) 40Ni14 vs IS 11169 (Part 1) 35Ni5Cr2

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 40Ni14 (IS 11169 (Part 1):1984) and IS 11169 (Part 1) 35Ni5Cr2 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 40Ni14 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1), while IS 11169 (Part 1) 35Ni5Cr2 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1). IS 11169 (Part 1) 40Ni14 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 35Ni5Cr2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 11169 (Part 1) 40Ni14 vs IS 11169 (Part 1) 35Ni5Cr2 is a 74.3% match. As per mechanical properties, the match is 100%. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 11169 (Part 1) 40Ni14:
IS 4367 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
74.3%
MECHANICAL MATCH
100%
OVERALL
69.9%
Specifications
Property IS 11169 (Part 1) 40Ni14 IS 11169 (Part 1) 35Ni5Cr2
Standard IS 11169 (Part 1):1984 IS 11169 (Part 1):1984
Category Alloy Steel Alloy Steel
C (%) 0.35-0.45 0.30-0.40
Mn (%) 0.50-0.80 0.60-0.90
Si (%) 0.10-0.35 0.10-0.35
Ni (%) 3.20-3.60 1.00-1.50
Cr (%) <=0.30 0.45-0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 40Ni14 IS 11169 (Part 1) 35Ni5Cr2
Hardness, annealed <=190 HB <=190 HB
Typical Applications
IS 11169 (Part 1) 40Ni14
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
IS 11169 (Part 1) 35Ni5Cr2
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Can IS 11169 (Part 1) 40Ni14 Be Substituted With IS 11169 (Part 1) 35Ni5Cr2?
IS 11169 (Part 1) 40Ni14 and IS 11169 (Part 1) 35Ni5Cr2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 1) 40Ni14
0 active listings and RFQs →
IS 11169 (Part 1) 35Ni5Cr2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 40Ni14 and IS 11169 (Part 1) 35Ni5Cr2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 1) 40Ni14 be substituted with IS 11169 (Part 1) 35Ni5Cr2?
IS 11169 (Part 1) 40Ni14 and IS 11169 (Part 1) 35Ni5Cr2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.