Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 15C4C (IS 11169 (Part 1):2022) and BS 970 (Part 3) 045M10 (BS 970 (Part 3):1991) are both steel grades.
Both fall under the Carbon Steel category.
IS 11169 (Part 1) 15C4C is typically used for cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex a), while BS 970 (Part 3) 045M10 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (table 14).
IS 11169 (Part 1) 15C4C is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 3) 045M10 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, IS 11169 (Part 1) 15C4C vs BS 970 (Part 3) 045M10 is a 59.5% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 15C4C
BS 970 (Part 3) 045M10
Reduction of Area, as rolled (+AR)
>=58% (for information)
Not specified
Tensile Strength, as rolled (+AR)
<=460 MPa (over 5 to 100 mm)
Not specified
Typical Applications
IS 11169 (Part 1) 15C4C
Cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex A)
BS 970 (Part 3) 045M10
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (Table 14)
Key Differences
IS 11169 (Part 1) 15C4C specifies Al, Cr, Cu, Mo which are not specified for BS 970 (Part 3) 045M10.
Can IS 11169 (Part 1) 15C4C Be Substituted With BS 970 (Part 3) 045M10?
IS 11169 (Part 1) 15C4C and BS 970 (Part 3) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 1) 15C4C and BS 970 (Part 3) 045M10?
IS 11169 (Part 1) 15C4C specifies Al, Cr, Cu, Mo which are not specified for BS 970 (Part 3) 045M10.
Can IS 11169 (Part 1) 15C4C be substituted with BS 970 (Part 3) 045M10?
IS 11169 (Part 1) 15C4C and BS 970 (Part 3) 045M10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.