Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 15Cr3 (IS 11169 (Part 1):2022) and EN 10028-2 10CrMo9-10 (EN 10028-2:2017) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 15Cr3 is typically used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b), while EN 10028-2 10CrMo9-10 is commonly used for flat products for pressure purposes. IS 11169 (Part 1) 15Cr3 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10028-2 10CrMo9-10 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 1) 15Cr3 vs EN 10028-2 10CrMo9-10 is a 57.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 11169 (Part 1) 15Cr3:
IS 4367 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 4) 103Cr6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6
Match Breakdown
CHEMISTRY MATCH
57.7%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 11169 (Part 1) 15Cr3 EN 10028-2 10CrMo9-10
Standard IS 11169 (Part 1):2022 EN 10028-2:2017
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.08-0.14
Cr (%) 0.50-0.80 2.00-2.50
Cu (%) <=0.15 <=0.30
Mn (%) 0.40-0.60 0.40-0.80
Mo (%) <=0.05 0.90-1.10
Ni (%) <=0.15 Not specified
P (%) <=0.035 <=0.020
S (%) <=0.035 <=0.010
Si (%) 0.10-0.35 <=0.50
N (%) Not specified <=0.012
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 15Cr3 EN 10028-2 10CrMo9-10
Hardness, annealed (+AC) <=140 HBW Not specified
Tensile Strength Not specified 480-630 MPa
Yield Strength Not specified >=310 MPa
Elongation Not specified >=18%
Condition Not specified Usual delivery condition normalized and tempered (+NT), nominal thickness up to 16 mm; transverse direction, Yield Strength is ReH, Elongation is A
Typical Applications
IS 11169 (Part 1) 15Cr3
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
EN 10028-2 10CrMo9-10
Flat products for pressure purposes
Key Differences
Can IS 11169 (Part 1) 15Cr3 Be Substituted With EN 10028-2 10CrMo9-10?
IS 11169 (Part 1) 15Cr3 and EN 10028-2 10CrMo9-10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 1) 15Cr3
0 active listings and RFQs →
EN 10028-2 10CrMo9-10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 15Cr3 and EN 10028-2 10CrMo9-10?
IS 11169 (Part 1) 15Cr3 specifies Ni which is not specified for EN 10028-2 10CrMo9-10. EN 10028-2 10CrMo9-10 specifies N which is not specified for IS 11169 (Part 1) 15Cr3.
Can IS 11169 (Part 1) 15Cr3 be substituted with EN 10028-2 10CrMo9-10?
IS 11169 (Part 1) 15Cr3 and EN 10028-2 10CrMo9-10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.